Fluoropolymer extrusions based on novel combinations of process parameters and clay minerals
A process for extruding of products from fluoropolymers preferably shaped as rods or tubes which have unique physical and other properties resulting from the addition of nanoparticles under unique processing conditions while also utilizing accurate control of processing parameters such as time and temperature and others according to novel methods.
1. A process for forming a part comprising:
A. providing a fluoropolymer material;
B. adding a lubricant to the fluoropolymer material to form a mixture therewith;
C. adding nanoparticles to the mixture at a level of 1% to 10% by weight to form a nanoparticle reinforced fluoropolymer;
D. molding of the nanoparticle reinforced fluoropolymer into a preform shape; and
E. extruding of the preform shape into the desired final shape of the part.
2. A process as defined in claim 1 wherein the mixture formed by adding lubricant to the fluoropolymer material is in the form of a fluoropolymer paste.
3. A process as defined in claim 1 wherein providing of a fluoropolymer material comprises providing of a fluoropolymer in powder form.
4. A process as defined in claim 1 wherein said extruding of the preform shape into the desired final shape of the part comprises ram extrusion.
5. The process as defined in claim 4 wherein said ram extrusion is performed at a processing pressure of approximately 1,000 to 75,000 pounds per square inch.
6. A process as defined in claim 1 wherein said adding a lubricant to the fluoropolymer material and said adding nanoparticles to the mixture is performed simultaneously.
7. The process as defined in claim 1 further comprising heating of the final part subsequent to extruding thereof.
8. The process as defined in claim 7 wherein said heating is of a sufficient temperature and time duration to flash the lubricant from the extruded final part.
9. The process as defined in claim 7 wherein said heating is performed in several individual stages at different temperature levels.
10. The process as defined in claim 7 wherein said heating is of a sufficient temperature and time duration for sintering of the extruded final part.
11. The process for forming a part as defined in claim 2 wherein the adding of the lubricant to the fluoropolymer paste is performed at a concentration level of 10% to 40% by weight.
12. The process for forming a part as defined in claim 2 further comprising rolling of the mixture of fluoropolymer paste and lubricant prior to the adding of nanoparticles thereto.
13. The process for forming a part as defined in claim 2 further comprising rolling of the mixture of fluoropolymer paste and lubricant after said adding of nanoparticles thereto.
14. The process for forming a part as defined in claim 12 wherein said rolling of the mixture is performed for a time period of between 1 and 24 hours at a temperature of less than 65 degrees Fahrenheit.
15. The process for forming a part as defined in claim 2 further comprising aging of the mixture of fluoropolymer paste and lubricant prior to adding of nanoparticles thereto for a period of time between 4 and 8 days at a temperature of between 60 and 90 degrees Fahrenheit.
16. The process as defined in claim 1 further comprising heating of the preform shape to 200 degrees Centigrade during extruding thereof to facilitate extruding thereof.
17. The process as defined in claim 2 wherein the nanoparticles are added at about 3% by weight.
18. The process as defined in claim 1 wherein the preform shape is a rod and wherein the desired final shape of the part is a rod.
19. The process as defined in claim 18 wherein the outside diameter of the desired final shape is 0.005 inches to 5.000 inches.
20. The process as defined in claim 1 wherein the preform shape is tubular and wherein the desired final shape of the part is tubular.
21. The process as defined in claim 20 wherein the outside diameter of the desired final shape is 0.005 inches to 5.000 inches.
22. The process as defined in claim 20 wherein the wall thickness of the tubular shape of the final part is from 0.0007 inches to about 4.0000 inches.
23. The process as defined in claim 2 wherein said providing of the fluoropolymer paste comprises providing of a poly(tetrafluoroethylene) paste.
24. The process as defined in claim 2 wherein said providing of the fluoropolymer material includes a comonomer component therewith.
25. The process as defined in claim 2 wherein said adding nanoparticles comprises adding minerals from the smectite family.
26. The process as defined in claim 2 wherein said adding nanoparticles comprises adding montmorillonite clay.
27. The process as defined in claim 2 wherein said adding nanoparticles comprises adding synthetic hectorite.
28. The process as defined in claim 25 wherein the minerals in the smectite family includes clays that contain fluorine group components.
29. The process as defined in claim 25 wherein the minerals added from the smectite family are surface treated with a coating.
30. The process as defined in claim 29 further comprising sintering of the extrudate subsequent to extruding thereof to facilitate removal and degradation of the coating on the minerals therewithin.
31. The process as defined in claim 2 further comprising heating of the extrudate subsequent to extruding for sintering thereof.
32. The process as defined in claim 2 wherein said extruding of the preform shape includes stretching of the nanoparticle reinforced fluoropolymer paste to increase the alignment of the molecular orientation thereof.
33. The process as defined in claim 2 wherein said adding of a lubricant comprises adding of a hydrocarbon fluid thereto.
34. The process as defined in claim 2 wherein said adding of a lubricant comprises adding of naphtha thereto.
35. The process as defined in claim 2 wherein said adding of the lubricant is performed at a temperature of less than 65 degrees Fahrenheit.
36. The process as defined in claim 2 wherein the desired final shape of the part is a rod and wherein an outer layer of virgin PTFE is pressed thereon to form a dual layer rod configuration with a nanocomposite reinforced fluoropolymer rod core and a virgin PTFE cuter layer bonded thereover to facilitate providing of a fusion rod used in the construction of catheters.
37. The process as defined in claim 2 wherein the final shape of the extruded part is a tube of nanoparticle reinforced fluoropolymer and wherein a rod of virgin PTFE is pressed within the center of the tube to form a rod-shaped configuration having a nanoparticle reinforced fluoropolymer outer skin and a virgin PTFE inner core bonded together by pressing to facilitate providing of a fusion rod.
38. The process as defined in claim 2 wherein the desired final shape of the part is a composite dual layer tube including an inner tubular layer and an outer tubular layer pressed thereover having an outside diameter between 0.005 inches and 5.000 inches.
39. The process as defined in claim 38 wherein the inner tubular layer is of a virgin PTFE and the outer tubular layer is of nanocomposite reinforced fluoropolymer.
40. The process as defined in claim 38 wherein the inner tubular layer is of a nanocomposite reinforced fluoropolymer and the outer tubular layer is of virgin FTFE.
41. The process as defined in claim 20 further comprising expanding of the tubing after extruding thereof to produce an expanded tubing which will be capable of shrinking back responsive to being exposed to heat and having enhanced shrink back capabilities.
42. A process for forming a part comprising:
A. providing a melt-processible fluoropolymer material;
B. adding nanoparticles to the material at a level of 1% to 10% by weight to form a fluoropolymer melt material which is nanoparticle reinforced and melt-processible; and
C. extruding of the fluoropolymer melt material into a desired final shape of the part.
43. The process as defined in claim 42 wherein said extruding includes melting of the nanoparticle reinforced melt-processible fluoropolymer melt material.
44. The process as defined in claim 42 wherein the fluoropolymer melt material is selected from the group consisting of FEP, PVF, PVDF, PFA, THV, PCTFE and MFA.
45. The process as defined in claim 42 wherein adding nanoparticles is performed at approximately 4% by weight.
46. The process as defined in claim 42 wherein the nanoparticle reinforced melt-processible fluoropolymer is formed from a mixture of pellet blends of 90% virgin FEP and 10% reinforced fluoropolymer to facilitate lower extruding temperatures and enhancing melting characteristics thereof.
47. The process as defined in claim 42 wherein the desired final shape of the part is lay flat tubing with an outside diameter of 0.010 inches to 10.000 inches having enhanced electrostatic dissipative properties.
48. The process as defined in claim 42 wherein said adding nanoparticles includes adding of minerals of the smectite family.
49. The process as defined in claim 48 wherein said adding nanoparticles includes adding at least one montmorillonite clay.
50. The process as defined in claim 48 wherein said adding nanoparticles includes adding at least one synthetic hectorite.
51. The process as defined in claim 48 wherein the mineral of the smectite family includes a surface coating for enhancing dispersing thereof.
52. The process as defined in claim 48 wherein the minerals in the smectite family includes clays that contain fluorine group components.
53. The process as defined in claim 42 wherein said extruding of the nanoparticle reinforced melt-processible fluoropolymer melt material includes stretching thereof in a controlled manner to increase alignment of the molecular orientation thereof.
54. The process as defined in claim 42 wherein said extruding of the nanoparticle reinforced melt-processible fluoropolymer forms a rod as the desired final shape of the part having an outside diameter of between about 0.005 inches to about 5.000 inches.
55. The process as defined in claim 42 wherein said extruding of the nanoparticle reinforced melt-processible fluoropolymer forms a tube as the desired final shape of the part having an outside diameter of between about 0.005 inches to about 5.000 inches.
56. The process as defined in claim 42 wherein said extruding of the fluoropolymer melt material forms a lay flat tubing having an outside diameter of between about 0.010 inches to about 10.000 inches with enhanced electrostatic dissipative properties.