Method for manufacturing optical fiber preforms
View Patent ↗Method and burner for increasing the deposition rate of porous glass deposit in the manufacture of optical preforms, by modifying the cross-sectional shape of the flow of glass particles impacting onto a target preform. In particular, the cross-section of the flow of glass particles is modified by increasing the dimension of the flow from a circular cross-section to one having a major and minor axis in a direction substantially perpendicular to the longitudinal axis of the target preform.
1. A method for producing an optical preform which comprises:
(a) feeding a flow of glass precursor material into a deposition burner and conferring to said flow a substantially circular cross-section;
(b) feeding a flow of combustible gas and a flow of combustion sustaining gas into said burner, in order to create a flame for uniformly heating said flow of glass precursor material and causing said glass precursor material to react, thereby forming a flow of fine glass particles;
(c) directing said flow of fine glass particles and said flame toward a target preform having an initial diameter; and
(d) causing said flow of glass particles to impact onto said target preform, thus increasing the radial dimensions of said preform up to a final diameter;
wherein the cross-section of at least the terminal portion of said flow impacting onto the target preform is modified into a cross-sectional shape having a major axis and a minor axis, said major axis being substantially orthogonal to the longitudinal axis of the target preform.
2. The method according to claim 1 , wherein said flame has a substantially circular cross-section which uniformly encircles the flow of glass precursor material in correspondence with its respective circular cross-section portion.
3. The method according to claim 1 , which further comprises conferring also to a portion of said flame a cross-sectional shape having a major axis and a minor axis, said major axis being substantially orthogonal to the longitudinal axis of the target preform, in order to uniformly surround the corresponding modified portion of the flow of glass particles.
4. The method according to claim 3 , wherein said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles is at least 1.2 times longer than the minor axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles.
5. The method according to claim 3 , wherein the length of said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles is less than about 2.5 times the length of the minor axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles.
6. The method according to claim 3 , wherein said major and said minor axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles are in ratio of from about 1.25:1 to about 1.8:1.
7. The method according to claim 3 , wherein said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles is in a ratio of at least about 1:2 or higher with respect to the initial diameter of the growing preform.
8. The method according to claim 3 , wherein said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles is in a ratio of at least about 1:2.5 or higher with respect to the initial diameter of the growing preform.
9. The method according to claim 3 , wherein the ratio between said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles and the final diameter of the preform is lower than about 1:7.
10. The method according to claim 3 , wherein the ratio between said major axis of the cross-section of said portion of flame surrounding the modified portion of the flow of glass particles and the final diameter of the preform is lower than about 1:6.