View Patent ↗A poly(urea-ureathane) based on polydimethyl siloxane is prepared by reacting an amino-terminated polydimethyl siloxane with polyisocyanate to form a prepolymer of poly(urea-urethane), and reacting the prepolymer and a chain extender in the presence of a catalyst. The resulting poly(urea-urethane) contains about 5-65 wt % of hard segments, and has a surface resistance of about 10-150 MΩ at high relative humidity, so that it can be used in anti-static electricity and electrostatic discharge shielding.
1. A process for preparing a polydimethyl siloxane-containing poly(urea-urethane) comprising the following steps:
a) reacting polydimethyl siloxane having two terminal amine groups with an excessive amount of polyisocyanate in an organic solvent to form a solution containing poly(urea-urethane) prepolymer; and
b) reacting the poly(urea-urethane) prepolymer from step a) with a chain extender in the presence of a catalyst to obtain a solution containing poly(urea-urethane);
introducing the poly(urea-urethane)-containing solution into an open mold, and evaporating the organic solvent contained therein to form a poly(urea-urethane) film, wherein said mold is made of aluminum enabling a water contact angle of an air-contact face of the poly(urea-urethane) film being 20-30 degrees smaller than that of a mold-contact face of the poly(urea-urethane) film.
2. The process according to claim 1 , wherein said chain extender is selected from a group consisting of ethylene glycol, glycerol, 2,2-bis(hydroxymethyl)propionic acid, and a mixture thereof.
3. The process according to claim 1 , wherein, based on the weight of the poly(urea-urethane), the poly(urea-urethane) prepared in step b) contains 25-50 wt % of a soft segment of polydimethyl siloxane.