Method of forming a nanocomposite coating
View Patent ↗There is disclosed a method of depositing a nanocomposite coating of stainless steel and a metallic carbide or metallic nitride, e.g. chromium carbide or chromium nitride, onto a stainless steel substrate 10 , including the steps of (a) providing the stainless steel substrate 10 ; (b) depositing stainless steel on the substrate 10 ; (c) depositing chromium carbide or chromium nitride on the substrate 10 ; and allowing a nanocomposite coating 14 of the stainless steel and chromium carbide or chromium nitride to form on the substrate 10.
1. A method of depositing a nanocomposite coating onto a metal or substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate;
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals along whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed interstitially, and wherein said substrate is made at least principally of stainless steel, copper, aluminum, magnesium, titanium, or an alloy of any of these metals.
2. A method according to claim 1 wherein said substrate is of substantially the same hardness as the stainless steel to be deposited on said substrate.
3. A method according to claim 1 wherein said first metal is chromium, tungsten, tantalum, or titanium.
4. A method according to claim 1 further including the step of providing a source of stainless steel for deposition on said at least one substrate.
5. A method according to claim 1 further including the step of providing a source of said first metal.
6. A method of depositing a nanocomposite coating onto a metal or metal alloy substrate including the steps of:
(a) providing at least one metal or metal alloy substrate;
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals along whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the step of providing a source of both said first metal and said stainless steel for deposition on said at least one substrate, wherein said source of both said first metal and said stainless steel for deposition on said substrate is an alloy of stainless steel and said first metal, and further including the step of reactively co-sputtering stainless steel and atoms of said first metal.
7. A method of depositing a nanocomposite coating onto a metal or metal alloy substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate;
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals alone whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the step of forming a layer of a second metal between said substrate and said nanocomposite coating.
8. A method according to claim 7 wherein said second metal is titanium, zirconium, hafnium or vanadium.
9. A method according to claim 7 wherein said layer of second metal is of a thickness of substantially 0.01 to 0.20 microns.
10. A method of depositing a nanocomposite coating onto a metal or metal alloy substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate:
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals alone whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the step of providing a source of carbon, wherein said source of carbon is a hydrocarbon gas.
11. A method according to claim 10 wherein said hydrocarbon gas is methane or acetylene.
12. A method of depositing a nanocomposite coating onto a metal alloy substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate:
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals along whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the step of providing a source of nitrogen.
13. A method according to claim 12 wherein said source of nitrogen is nitrogen gas or ammonia.
14. A method of depositing a nanocomposite coating onto a metal or metal alloy substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate:
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals alone whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the step of negatively biasing said at least one substrate during deposition of stainless steel and said carbide or nitride of said first metal.
15. A method according to claim 14 wherein the biasing voltage is between of −20 volts to −200 volts.
16. A method of depositing a nanocomposite coating onto a metal or metal alloy substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate:
(b) depositing stainless steel on said at least one substrate;
(c) depositing a carbide or nitride of a first metal on said at least one substrate; and
(d) allowing a nanocomposite coating of said stainless steel and carbide or nitride of said first metal to form on said at least one substrate, wherein the nanocomposite coating includes grains of stainless steel crystals along whose grain boundaries a nano-structure of molecules of metallic carbide or metallic nitride is formed insterstitially, further including the steps of:
(e) placing said at least one substrate at a first location for deposition of stainless steel thereon;
(f) placing said at least one substrate at a second location for deposition of said carbide or nitride of said first metal thereon; and
(g) moving said at least one substrate away from said first and second locations to allow a nanocomposite coating of said stainless steel and said carbide or nitride of said first metal to form on said at least one substrate.
17. A method according to claim 16 further including the step of placing said at least one substrate at a third location for deposition of a second metal thereon before placing said at least one substrate at said first location and said second location.
18. A metal or metal alloy article deposited with a nanocomposite coating according to the method of claim 1 .
19. A method of forming a coating onto a metal or substrate, including the steps of:
(a) providing at least one metal or metal alloy substrate; and
(b) vapor depositing stainless steel and a carbide or nitride of a first metal on said at least one metal or metal alloy substrate to form grains of stainless steel interspersed with molecules of the carbide or nitride of the first metal along the grain boundaries of the stainless steel on said at least one metal or metal alloy substrate.
20. A method according to claim 19 , further including the step of forming a layer of a titanium, zirconium, hafnium or vanadium between said substrate and said coating, wherein optionally said layer of second metal is of a thickness of substantially 0.01 to 0.20 microns.
21. A method according to claim 19 , further including the step of providing a hydrocarbon gas, nitrogen gas or ammonia, and/or further including the step of negatively biasing said at least one substrate during deposition of stainless steel and said carbide or nitride of said first metal.