Glass fiber-reinforced thermoplastic resin pellets and their production process
View Patent ↗A process for producing glass fiber-reinforced thermoplastic resin pellets, which comprises a step of drawing out glass fiber strands from the inside of glass fiber rolls and introducing them into a resin impregnation die, a step of supplying a molten thermoplastic resin into the resin impregnation die and impregnating the glass fiber strands with the thermoplastic resin, a step of drawing out the glass fiber strands impregnated with the thermoplastic resin from the resin impregnation die and cooling and solidifying the thermoplastic resin to obtain a linear molded product, and a step of cutting the molded product into a predetermined length, wherein as the glass fibers, glass fiber strands drawn out from rolls, each roll obtained by bundling monofilaments having a diameter of from 6 to 25 μm and winding them so that the inner diameter will be from 18 to 50 cm, are used.
1. A process for producing glass fiber-reinforced thermoplastic resin pellets, which comprises a step of drawing out glass fiber strands from the inside of glass fiber rolls and introducing them into a resin impregnation die, a step of supplying a molten thermoplastic resin into the resin impregnation die and impregnating the glass fiber strands with the thermoplastic resin, a step of drawing out the glass fiber strands impregnated with the thermoplastic resin from the resin impregnation die and cooling and solidifying the thermoplastic resin to obtain a linear molded product, and a step of cutting the molded product into a predetermined length, wherein as the glass fibers, glass fiber strands drawn out from rolls, each roll obtained by bundling monofilaments having a diameter of from 6 to 25 μm and winding them so that the inner diameter will be from 18 to 50 cm, are used.
2. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein each roll is obtained by winding a glass fiber strand into a drum shape while traversing the strand by means of a spiral wire.
3. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the roll width of each roll is from 10 to 60 cm.
4. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the number of the monofilaments bundled per one glass fiber strand is at most 1,200.
5. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the count (TEX:g/1,000 m) per one glass fiber strand is from 150 to 500.
6. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the glass fiber content in the pellets is from 30 to 85 mass %.
7. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the number of the glass fiber strands contained in the pellets is from 3 to 35.
8. The process for producing glass fiber-reinforced thermoplastic resin pellets according to claim 1 , wherein the twist multiplier TM of the glass fiber strand drawn out from each roll satisfies the following formula:
TM=((denier:g/9,000 m) 1/2 ×(number of twist per 1 m))/287.4,
0.076 ≦TM≦ 0.350.
9. Glass fiber-reinforced thermoplastic resin pellets which are produced by the process as defined in claim 1 , wherein the glass fibers are substantially continuous over the entire longitudinal direction of the pellets and are aligned almost in parallel with one another.
10. A roll for glass fiber-reinforced thermoplastic resin pellets, wherein the twist multiplier TM of a glass fiber strand drawn out from the roll satisfies the following formula:
TM =((denier:g/9,000 m) 1/2 ×(number of twist per 1 m))/287.4,
0.076 ≦TM≦ 0.350.