Adhesive composition
View Patent ↗The invention relates to an adhesive composition comprising (i) one or more styrenic block copolymers, (ii) a tackifier resin, and (iii) one or more plasticizers, wherein the or one of the styrenic block copolymers is of the general formulae A-C-A, (1) or (A-C) n -X, (2) wherein each A independently is a polymer block of an aromatic vinyl compound, and C is a mixed polymer block (B/I) of butadiene (B) and isoprene (I) in a weight ratio B:I in the range of 30:70 to 70:30, and said polymer block C has a glass transition temperature (Tg) of at most −50° C. (determined according to ASTM E-1356-98), n is an integer equal to or greater than 2, and X is the residue of a coupling agent, and wherein the tackifier resin has an aromaticity (in relative percentage of aromatic protons as determined by H-NMR) in the range of from 3 to 18%.
1. An adhesive composition consisting essentially of (i) one or more styrenic block copolymers, (ii) a mixed aliphatic/aromatic hydrocarbon tackifier resin, and (iii) one or more plasticizers, wherein said styrenic block copolymer is of the general formulae
A-C-A
or
(A-C) n -X,
wherein each A independently is a polymer block of an aromatic vinyl compound, and C is a mixed polymer block (B/I) of butadiene (B) and isoprene (I) in a weight ratio B:I in the range of 30:70 to 70:30, and said polymer block C has a glass transition temperature (Tg) of at most −50° C. (determined according to ASTM E-1356-98), n is an integer equal to or greater than 2, and X is the residue of a coupling agent,and wherein the tackifier resin has an aromaticity (in relative percentage of aromatic protons as determined by H-NMR) of 4.2%.
2. The adhesive composition of claim 1 , wherein polymer block C has average homopolymer block lengths pB respectively pI of less than 100 monomer units.
3. The adhesive composition of claim 2 , wherein the aromatic vinyl compound is styrene.
4. The adhesive composition of claim 3 , wherein the proportion of bound aromatic vinyl compound is in the range from 10 to 50 weight percent.
5. The adhesive composition of claim 4 , wherein the proportion of bound butadiene is in the range from 15 to 65 weight percent.
6. The adhesive composition of claim 5 , wherein the proportion of bound isoprene is in the range from 15 to 65 weight percent.
7. The adhesive composition of claim 6 , wherein each A polymer block has a true molecular weight in the range of 9,500 to 25,000.
8. The adhesive composition of claim 6 , wherein the C polymer block has a vinyl content of less than 15 weight percent.
9. An adhesive composition of claim 8 , wherein the block copolymer has a weight average molecular weight (expressed in terms of polystyrene) in the range of 100,000 to 500,000 (as determined by GPC).
10. An adhesive composition of claim 9 , wherein component (i) comprises a block copolymer according to general formulae A-C-A or (A-C)n-X, and a diblock copolymer A-B in a weight ratio of block copolymer:diblock in the range of 100/0 to 30/70.
11. The adhesive composition of claim 3 wherein said plasticizer is a low aromatic content hydrocarbon oil.
12. The adhesive composition of claim 11 wherein said composition comprises 100 parts by weight of said block copolymer and 50 to 400 parts by weight of said tackifying resin.
13. The adhesive composition of claim 12 wherein said composition comprises 5 to 150 parts by weight of said plasticizer.
14. An adhesive composition comprising (i) one or more styrenic block copolymers, (ii) a mixed aliphatic/aromatic hydrocarbon tackifier resin, and (iii) one or more plasticizers, wherein said styrenic block copolymer is of the general formulae
A-C-A
or
(A-C) n -X,
wherein each A independently is a polymer block of an aromatic vinyl compound, and C is a mixed polymer block (B/I) of butadiene (B) and isoprene (I) in a weight ratio B:I in the range of 30:70 to 70:30, and said polymer block C has a glass transition temperature (Tg) of at most −50° C. (determined according to ASTM E-1356-98), n is an integer equal to or greater than 2, and X is the residue of a coupling agent, and wherein the tackifier resin has an aromaticity (in relative percentage of aromatic protons as determined by H-NMR) of 4.2%.