Method for forming electroplating film on surfaces of articles
View Patent ↗An object of the present invention is to provide a method for forming a uniform and dense electroplating film with high adhesion strength on the surface of an article, yet irrespective of the surface material and the surface properties of the article. A means for a solution of the problem comprises: forming on the surface of the article, a resin coating made of a resin containing dispersed therein a powder of a first metal; then forming a second-metal substituted plating film on the surface of the resin coating by immersing the resin-coated article in a solution containing ions of a second metal having an ionization potential nobler than that of the first metal; and further forming an electroplating film of a third metal on the surface of the metal-substituted plating film.
1. A method for forming an electroplating film on the surface of a rare earth permanent magnet, which comprises: forming on the surface of the magnet, a resin coating made of a resin containing dispersed therein a powder of a first metal; then forming a second-metal substituted plating film on the surface of the resin coating by immersing the resin-coated magnet in a solution containing ions of a second metal having an ionization potential nobler than that of the first metal; and further forming an electroplating film of a third metal on the surface of the metal-substituted plating film, wherein the resin coating is a non-conductive coating, the second metal and the third metal are the same, and the step of forming the substituted plating film and the step of forming the electroplating film are carried out in the same plating bath.
2. A method for forming an electroplating film as claimed in claim 1 , wherein the rare earth permanent magnet is a bonded magnet.
3. A method for forming an electroplating film as claimed in claim 1 , wherein the volume resistivity of the non-conductive coating is 1×10 4 Ω·cm or higher.
4. A method for forming an electroplating film as claimed in claim 1 , wherein the powder of the first metal is dispersed in the resin coating at a content in a range of from 50 wt% to 99 wt%.
5. A method for forming an electroplating film as claimed in claim 1 , wherein the average particle diameter of the powder of the first metal is in a range of from 0.001 μm to 30 μm.
6. A method for forming an electroplating film as claimed in claim 1 , wherein the film thickness of the resin coating is in range of from 1 μm to 100 μm.
7. A method for forming an electroplating film as claimed in claim 1 , wherein the first metal is zinc and the second metal is nickel or tin.
8. A method for forming an electroplating film as claimed in claim 1 , wherein the first metal is nickel and the second metal is copper.
9. A method for forming an electroplating film as claimed in claim 1 , wherein the film thickness of the substituted plating film is in a range of from 0.05 μm to 2 μm.