Method for producing granulated powder of R—FE—B type alloy and method for producing R—FE—B type alloy sintered compact
View Patent ↗The method for producing a granulated powder of the present invention includes the steps of: preparing an R—Fe—B alloy powder; and granulating the alloy powder using at least one kind of granulating agent selected from normal paraffins, isoparaffins and depolymerized oligomers, to prepare a granulated powder. The produced R—Fe—B alloy granulated powder is excellent in flowability and compactibility as well as in binder removability.
1. A method for producing a granulated powder of an R—Fe—B alloy, comprising the steps of:
preparing an R—Fe—B alloy powder; and
granulating a mixture consisting of the alloy powder and at least one kind of granulating agent selected from a group consisting of normal paraffins, isoparaffins and depolymerized oligomers and optionally a terpene resin or an aliphatic resin to prepare a granulated powder;
wherein the at least one kind of granulating agent is added in the step of granulating in an amount of 0.1 mass% to 50 mass% with respect to the mass of the granulated powder;
wherein the mean particle size of the alloy powder is in the range of 1.5 μm to 5 μm;
wherein the mean molecular weight of the at least one kind of granulating agent is in the range of 120 to 500; and
wherein the granulated powder is prepared by a fluidized bed granulation process.
2. The method for producing a granulated powder of an R—Fe—B alloy of claim 1 , wherein the at least one kind of granulating agent is normal paraffin and/or isoparaffin having a boiling point in a range of 80° C. to 250° C.
3. The method for producing a granulated powder of an R—Fe—B alloy of claim 1 , wherein the mean particle size of the granulated powder is in a range of 0.05 mm to 3.0 mm.
4. A method for producing an R—Fe—B alloy sintered body comprising the steps of:
producing a granulated powder by the method for producing a granulated powder of an R—Fe—B alloy of claim 1 ;
compacting an R—Fe—B alloy powder material including the granulated powder in a state of being aligned under application of a magnetic field, to form a compact; and
sintering the compact.
5. The method for producing an R—Fe—B alloy sintered body of claim 4 , wherein the step of sintering comprises the step of heating the compact in an inert gas atmosphere or in a vacuum, and also serves as the step of removing the granulating agent.
6. The method for producing an R—Fe—B alloy sintered body of claim 4 , wherein the powder material substantially includes only the granulated powder.