Polymers containing bioactive glass with antimicrobial effect
View Patent ↗The method of protecting a polymeric plastic from attack by bacteria and fungi includes providing bioactive glass particles having a mean particles size preferably less than 2 μm as an additive incorporated into the polymeric plastic. The bioactive glass particles contain 40 to 60% by weight of SiO 2 , 10 to 30% by weight of CaO, 10 to 35% by weight of Na 2 O, 2 to 8 % by weight of P 2 O 5 , 0 to 25% by weight of CaF 2 , 0 to 10% by weight of B 2 O 3 , 0 to 8% by weight of K 2 O and/or 0 to 5% by weight of MgO. The additive is included in amounts of up to 25% by weight in the polymeric plastic.
1. A polymer additive with antimicrobial action, said polymer additive comprising a polymeric carrier and from 30 to 90% by weight of bioactive glass particles with a mean particle size less than 2 microns, wherein said bioactive glass particles contain:
SiO 2 40-60 wt. %
CaO 10-30 wt. %
Na 2 O 10-35 wt. %
P 2 O 5 2-8 wt. %
CaF 2 0-25 wt. %
B 2 O 3 0-10 wt. %
K 2 O 0-8 wt. %
MgO 0-5 wt. %.
2. The polymer additive as defined in claim 1 , containing from 30 to 50% by weight of said bioactive glass particles.
3. The polymer additive as defined in claim 1 , wherein a molar ratio of calcium oxide to phosphorus oxide is greater than 2 and less than 10.
4. The polymer additive as defined in claim 1 , wherein said polymeric carrier comprises a PGA biodegradable polymer, LGA biodegradable polymer, polyamide polymer, polycarbonate polymer, polyester polymer, polyimide polymer, polyurea polymer, polyurethane polymer, organic fluoropolymer, polyacrylamide polymer, polyacrylic acid polymer, polyacrylates polymer, polymethacrylates polymer, polyolefin polymer, polystyrene polymer, polystyrene copolymer, polyvinyl ester polymer, polyvinyl ether polymer, polyvinylidene chloride polymer, vinyl polymer, polyoxymethylene polymer, polyaziridine polymer, polyoxyalkylene polymer, polyethylene polymer, electrically conductive polymer, high-temperature polymer, polyphenylene oxide polymer, collagen, fibrin, chitin, chitosan, cellulose, cellulose ester, cellulose ether, enzyme polymer, polynucleic acid, polysaccharide, protein, silk polymer, starch polymer, or wool polymer.
5. A polymer additive with antimicrobial action, said polymer additive consisting of bioactive glass particles with a mean particle size less than 2 microns, wherein said bioactive glass particles contain:
SiO 2 40-60 wt. %
CaO 10-30 wt. %
Na 2 O 10-35 wt. %
P 2 O 5 2-8 wt. %
CaF 2 0-25 wt. %
B 2 O 3 0-10 wt. %
K 2 O 0-8 wt. %
MgO 0-5 wt. %.
6. The polymer additive as defined in claim 5 , wherein a molar ratio of calcium oxide to phosphorus oxide is greater than 2 and less than 10.
7. A polymer containing 1 to 30% by weight of bioactive glass particles having antimicrobial action, wherein said bioactive glass particles have a mean particle size less than 2 microns and contain:
40 to 60% by weight of SiO 2 ,
10 to 30% by weight of CaO,
10 to 35% by weight of Na 2 O,
2 to 8% by weight of P 2 O 5 ,
0 to 25% by weight of CaF 2 ,
0 to 10% by weight of B 2 O 3 ,
0 to 8% by weight of K 2 O, and/or
0 to 5% by weight of MgO.
8. The polymer as defined in claim 7 , containing from 1 to 10% by weight of said bioactive glass particles.
9. A method of protecting a plastic comprising a polymer from attack by bacteria and fungi, said method comprising including bioactive glass particles in said plastic as an antimicrobial additive, said bioactive glass particles having a mean particle size less than 2 microns and containing:
40 to 60% by weight of SiO 2 ,
10 to 30% by weight of CaO,
10 to 35% by weight of Na 2 O,
2 to 8% by weight of P 2 O 5 ,
0 to 25% by weight of CaF 2 ,
0 to 10% by weight of B 2 O 3 ,
0 to 8% by weight of K 2 O, and/or
0 to 5% by weight of MgO.