Curing composition and method for applying alkyd coating material with the same
View Patent ↗An object of the present invention is to improve a drying property of paint in application of alkyd paint to the surface of a cured material resulting from the curable composition containing an oxyalkylene polymer having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond, and to provide a composition that contains an oxyalkylene polymer (A) having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond and 2,6-di-t-butylhydroxytoluene wherein the content of the above-described 2,6-di-t-butylhydroxytoluene is 350 ppm or less relative to the above-described polymer (A).
1. A composition comprising an oxyalkylene polymer (A) having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond and 2,6-di-t-butylhydroxytoluene,
wherein the content of 2,6-di-t-butylhydroxytoluene is controlled to be 1–31 ppm relative to the polymer (A) after the silicon-containing functional group is introduced therein.
2. A coating method comprising the step of applying alkyd paint to a surface of a cured material resulting from the composition according to claim 1 .
3. A composition according to claim 1 , which further comprises another antioxidant in addition to 2,6-di-t-butylhydroxytoluene.
4. A composition according to claim 1 , which further comprises macromolecular plasticizer, wherein the content of 2,6-di-t-butylhydroxytoluene is controlled to be 1–31 ppm relative to the total amount of said polymer (A) and said plasticizer.
5. A composition comprising an oxyalkylene polymer (A) having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond, a polymer (B) comprising a molecular chain composed of (meth)acrylate monomer units and comprising at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond, and 2,6-di-t-butylhydroxytoluene,
wherein the content of 2,6-di-t-butylhydroxytoluene is controlled to be 1–31 ppm relative to the total amount of the polymer (A) and the polymer (B) after the silicon-containing functional group is introduced therein.
6. A coating method comprising the step of applying alkyd paint to a surface of a cured material resulting from the composition according to claim 5 .
7. A composition according to claim 5 , which further comprises another antioxidant in addition to 2,6-di-t-butylhydroxytoluene.
8. A composition according to claim 5 , which further comprises macromolecular plasticizer, wherein the content of 2,6-di-t-butylhydroxytoluene is controlled to be 1 –31 ppm relative to the total amount of said polymer (A), said polymer (B), and said plasticizer.
9. A method for improving a drying property of alkyd paint in application of the alkyd paint to a surface of a cured material resulting from a composition comprising an oxyalkylene polymer (A) having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond and 2,6-di-t-butylhydroxytoluene, the method comprising the step of:
adjusting the content of 2,6-di-t-butylhydroxytoluene to be controlled at 1–31 ppm relative to the polymer (A) after the silicon-containing functional group is introduced therein.
10. A method for improving a drying property of alkyd paint in application of the alkyd paint to the surface of a cured material resulting from a composition comprising an oxyalkylene polymer (A) having at least one silicon-containing functional group capable of cross-linking by formation of at least one siloxane bond, a polymer (B) comprising a molecular chain composed of (meth)acrylate monomer units and comprising silicon-containing functional groups capable of cross-linking by formation of siloxane bonds, and 2,6-di-t-butylhydroxytoluene, the method comprising the step of:
adjusting the content of 2,6-di-t-butylhydroxytoluene to be controlled at 1–31 ppm relative to the total amount of the polymer (A) and the polymer (B) after the silicon-containing functional group is introduced therein.