Magnesium-based alloy wire and method of its manufacture
View Patent ↗Magnesium-based alloy wire excelling in strength and toughness, its method of manufacture, and springs in which the magnesium-based alloy wire is utilized are made available. The magnesium-based alloy wire contains, in mass %, 0.1 to 12.0% Al, and 0.1 to 1.0% Mn, and is provided with the following constitution. Diameter d that is 0.1 mm or more and 10.0 mm or less; length L that is 1000 d or more; tensile strength that is 250 MPa or more; necking-down rate that is 15% or more; and elongation that is 6% or more. Such wire is produced by draw-forming it at a working temperature of 50° C. or more, and by heating it to a temperature of 100° C. or more and 300° C. or less after the drawing process has been performed.
1. Magnesium-based alloy wire of composition containing, in mass %, 0.1 to 12.0% Al, and 0.1 to 1.0% Mn; the magnesium-based alloy wire being manufactured by a procedure including a drawing process of drawing a parent material of said composition at a controlled temperature to work the parent material into wire form so as to impact the following properties to the magnesium-based alloy wire:
a length L of 1000 d or more, where d is its diameter;
a tensile strength of 250 MPa or more;
a necking-down rate of 15% or more;
a elongation of 6% or more;
a crystal grain size of said composition of between 3.5 μm and 10 μm inclusive; and
a surface roughness of R z≦ 10 μm.