View Patent ↗Alkaline electrochemical cells with substantially increased performance characteristics have a porous anode, with a porosity equal to or greater than 69%, and a porous cathode, comprising manganese dioxide and having a porosity equal to or greater than 26%.
1. An electrochemical cell comprising an aqueous alkaline electrolyte, a porous cathode, and a porous anode, wherein the cathode comprises manganese dioxide, the cathode porosity is equal to or greater than 26% and not greater than 36%, the anode comprises an electrochemically active material insoluble in the electrolyte, the anode porosity is equal to or greater than 69% and not greater than 76%, and the electrolyte comprises KOH in a concentration prior to discharge selected such that, after the cell has been discharged to reduce the manganese in the manganese dioxide to Mn +3.0 , the calculated KOH concentration is about 50% w/w.
2. A cell according to claim 1 , wherein the cathode porosity is at least 27%.
3. A cell according to claim 2 , wherein the cathode porosity is at least 28%.
4. A cell according to claim 1 , wherein the cathode porosity is no greater than 34%.
5. A cell according to claim 1 , wherein the anode porosity is at least 70%.
6. A cell according to claim 1 , wherein the anode comprises zinc, and the zinc consists of zinc having a calculated overall tap density of less than 3.2 g/cc.
7. A cell according to claim 6 , wherein the maximum calculated overall tap density of the zinc is 3.19 g/cc when the anode porosity is 69% and 0.06 g/cc lower for every 1% increase in anode porosity over 69%.
8. A cell according to claim 6 , wherein the maximum calculated overall tap density of the zinc is 3.13 g/cc when the anode porosity is 69% and 0.085 g/cc lower for every 1% increase in anode porosity over 69%.
9. An electrochemical cell comprising an aqueous alkaline electrolyte, a porous cathode, and a porous anode, wherein the cathode comprises manganese dioxide, the cathode porosity is equal to or greater than 26% and not greater than 36%, the anode comprises an electrochemically active material insoluble in the electrolyte, the anode porosity is equal to or greater than 69% and not greater than 76%, the anode comprises zinc consisting of zinc having an overall tap density of from 2.83 to 2.96 g/cc, inclusive, and the anode porosity is about 71%.
10. A cell according to claims 6 , wherein the zinc comprises at least 4% by weight uniformly shaped, low-density zinc particles having a tap density less than 2.5 g/cc.
11. A cell according to claim 10 , wherein the uniformly shaped, low density zinc is zinc flake and the flake thickness dimension is at least 10 times smaller than the flake length and width dimensions.
12. A cell according to claim 11 , wherein the zinc has a zinc flake content of at least 1% w/w per 1% increase in porosity of the anode over 66%.
13. A cell according to claim 11 , wherein the uniformly shaped, low-density zinc forms at least 1.5% w/w per 1% porosity of the anode over 67%.
14. A cell according to claim 11 , wherein the uniformly shaped, low-density zinc forms at least 2% w/w per 1% porosity of the anode over 67%.
15. A cell according to claim 5 , wherein the anode comprises zinc, and the zinc has a zinc flake content of about 5 to 11 weight percent and the anode has a porosity of between 70 and 73%.
16. A cell according to claim 15 , wherein about 8% to 11% by weight of the zinc is zinc flake.
17. A cell according to claim 1 , wherein the ratio of the capacity of the anode to that of the cathode is between 1.15:1 and 1.25:1.
18. A cell according to claim 1 , wherein the cathode further comprises carbon and a manganese dioxide to carbon ratio is no higher than about 26:1.
19. A cell according to claim 18 , wherein the manganese dioxide to carbon ratio is between 20:1 and 25:1.
20. A cell according to claim 19 , wherein the manganese dioxide to carbon ratio is between 22:1 and 24:1.
21. A cell according to claim 19 , wherein the cathode porosity is 28 to 30%, inclusive, and the manganese dioxide to carbon ratio is between 20:1 and 23:1.
22. A cell according to claim 19 , wherein the cathode porosity is in excess of 30%.
23. A cell according to claim 1 , wherein the ratio cathode capacity: cell volume is in the range of 0.42 to 0.49 Ah/cm 3 , when the cathode capacity is calculated based upon reduction of all manganese in the manganese dioxide to Mn +3.0 .
24. An electrochemical cell comprising an aqueous alkaline electrolyte, a porous cathode, and a porous anode, wherein the cathode comprises manganese dioxide, the cathode porosity is equal to or treater than 26% and not greater than 36%, the anode comprises an electrochemically active material insoluble in the electrolyte, the anode porosity is equal to or greater than 69% and not greater than 76%, the electrolyte comprises KOH in a concentration prior to discharge selected such that, after the cell has been discharged to reduce the manganese in the manganese dioxide to Mn +3.0 the calculated KOH concentration is about 50% w/w, and the calculated final concentration of potassium hydroxide after reduction of the manganese in the manganese dioxide to Mn +3.0 is between 49.5 and 51.5% (w/w solution).