Propylene random copolymer and process for the production thereof
View Patent ↗The present invention relates to a process for preparing a propylene random copolymer comprising polymerisation of propylene with a comonomer, said comonomer being ethylene or an α-olefin comprising at least four carbon atoms, in the presence of a catalyst in a muiltistage process comprising polymerisation of propylene with a comonomer in a first reaction zone including at least one slurry reactor to give a first polymerisation product, transferring said first product to a second reaction zone including at least one gas phase reactor and polymerisations of propylene with a comonomer in said gas phase reactor in the presence of said first polymerisation product, wherein the temperature in the gas phase reactor is at least 10° C. higher than in the slurry reactor and to a polymer obtainable by this process. Furthermore, the invention relates to a propylene random copolymer prepared by copolymerisation of propylene with a comonomer wherein the distribution of the comonomer determined according to the TREF method is multimodal, preferably bimodal, a peopylene radom copolymer prepared by copolymerisation of propylene with a comonomer wherein the copolymer is having an elution interval determined according to the TREF method of 50° C. or more, a propylene random copolymer prepared by copolymerisation of propylene with a comonomer, wherein the random copolymer is a unimodal polymer and the elution interval determined by the TREF method is given by the equation Y≦4.5.m+16 wherein Y is the elution interval in ° C. and m is the percentage of ethylene in the copolymer in wt. %, and to the use of such a copolymers for the production of a film, of an article by blow moulding or injection moulding, of a fibre or of a pipe.
1. A process for preparing a propylene random copolymer comprising propylene and a comonomer, said comonomer being ethylene or an α-olefin comprising at least four carbon atoms, the process comprising:
polymerising a first amount of the propylene with a first amount of the comonomer in the presence of a catalyst in a first reaction zone including at least one slurry reactor to give a slurry reactor product;
transferring the slurry reactor product to a second reaction zone including at least one gas phase reactor; and
polymerising a second amount of the propylene with a second amount of the comonomer in said gas phase reactor in the presence of the slurry reactor product to produce the propylene random copolymer, the propylene random copolymer consisting of the slurry reactor product and a gas phase product;
wherein the temperature in the gas phase reactor is at least 10° C. higher than the temperature in the slurry reactor, the temperature in the gas phase reactor is 80° C. or more, and the temperature in the slurry reactor is 70° C. or more; and
wherein the propylene random copolymer has a xylene solubles content of from 5 to 15 weight percent and an elution interval of 50° C. or more.
2. A process according to claim 1 wherein the temperature in said gas phase reactor is at least 15° C. higher than that in said slurry reactor.
3. A process according to claim 1 wherein the comonomer content of the gas phase product is higher than the comonomer content of the slurry reactor product.
4. A process according to claim 3 wherein the comonomer content of the gas phase product is at least 0.5 wt. % higher than the comonomer content of the slurry reactor product.
5. A process according to claim 1 wherein said comonomer is ethylene.
6. A process according to claim 5 wherein the ethylene content of the slurry reactor product is from 2 to 6 wt. %.
7. A process according to claim 5 wherein the ethylene content of the gas phase product is from 3 to 12 wt. %.
8. A process according to claim 1 wherein the slurry reactor is a bulk reactor.
9. process according to claim 1 wherein the temperature in the gas phase reactor is 85° C. or more.
10. process according to claim 1 wherein the production split between the slurry reactor and the gas phase reactor is from 30:70 to 70:30.
11. process according to claim 1 wherein the catalyst is a Zlegler-Natta type catalyst system including a catalyst component, a cocatalyst component and an external donor.
12. A process for preparing a propylene random copolymer comprising propylene and a comonomer, said comonomer being ethylene or an a-olefin comprising at least four carbon atoms, the process comprising:
polymerising a first amount of the propylene with a first amount of the comonomer in the presence of a catalyst in a first reaction zone including at least one slurry reactor to give a slurry reactor product;
transferring the slurry reactor product to a second reaction zone including at least one gas phase reactor; and
polymerising a second amount of the propylene with a second amount of the comonomer in said gas phase reactor in the presence of the slurry reactor product to produce the propylene random copolymer, the propylene random copolymer consisting of the slurry reactor product and a gas phase product;
wherein the temperature in the gas phase reactor is at least 10° C. higher than the temperature in the slurry reactor, the temperature in the gas phase reactor is 80° C. or more, and the temperature in the slurry reactor is 70° C. or more; and
wherein the propylene random copolymer has an elution interval of 50° C. or more.