Alkaline earth aluminate phosphor, phosphor paste composition and vacuum ultraviolet excitation light emitting element
View Patent ↗A phosphor improved against luminance deterioration with time under vacuum ultraviolet irradiation, a phosphor paste composition, and a vacuum ultraviolet excitation light emitting element high in luminance retaining rate and improved in luminance, are presented. An alkaline earth aluminate phosphor which is a phosphor represented by the formula a (M 1-x Eu x )O.6Al 2 O 3 (wherein M represents at least one alkaline earth metal element selected from the group consisting of Ba, Sr and Ca, and x and a satisfy 0<x<1 and O.9≦a≦1.8, respectively) and which has a wide-band peak over an angle region of diffraction angle (2θ) of from 28° to 31° in powder diffraction X-ray spectrum by CuKα1 characteristics X-ray, and a vacuum ultraviolet excitation light emitting element provided with a fluorescent layer made of the phosphor.
1. An alkaline earth aluminate phosphor which is a phosphor represented by the formula a(M 1-x Eu x )O•6Al 2 O 3 and which is characterized by having a wide-band peak over an angle region of diffraction angle (2θ) of from 28° to 31° in powder diffraction X-ray spectrum by CuKα1 characteristics X-ray of said phosphor, wherein in the above formula, M represents at least one alkaline earth metal element selected from the group consisting of Ba, Sr and Ca, and x and a represent numbers satisfying the conditions of 0<x<1 and 0.9≦a≦1.8 respectively.
2. The alkaline earth aluminate phosphor according to claim 1 , wherein the half value width of the wide-band peak is at least 0.50°.
3. A vacuum ultraviolet excitation light emitting element which comprises a vacuum envelope having a fluorescent layer formed inside and a rare gas sealed in the vacuum envelope so that the fluorescent layer is excited by vacuum ultraviolet rays radiated by discharge of the rare gas, to emit light, and wherein a vacuum ultraviolet excitation alkaline earth aluminate phosphor as defined in claim 2 is used for the fluorescent layer.
4. The alkaline earth aluminate phosphor according to claim 2 , wherein the integral value of the peak present over an angle region of diffraction angle (2θ) of from 28° to 31° in powder diffraction X-ray spectrum is at least 0.5 time the integral value of an independent peak present over an angle region of diffraction angle (2θ) of 21° to 22° of the spectrum.
5. A phosphor paste composition which comprises a phosphor dispersed in a solvent having a binder dissolved therein and wherein the phosphor is an alkaline earth aluminate phosphor as defined in claim 4 .
6. A vacuum ultraviolet excitation light emitting element which comprises a vacuum envelope having a fluorescent layer formed inside and a rare gas sealed in the vacuum envelope so that the fluorescent layer is excited by vacuum ultraviolet rays radiated by discharge of the rare gas, to emit light, and wherein a vacuum ultraviolet excitation alkaline earth aluminate phosphor as defined in claim 4 is used for the fluorescent layer.
7. A phosphor paste composition which comprises a phosphor dispersed in a solvent having a binder dissolved therein and wherein the phosphor is an alkaline earth aluminate phosphor as defined in claim 2 .
8. The alkaline earth aluminate phosphor according to claim 1 , wherein the integral value of the peak present over an angle region of diffraction angle (2θ) of from 28° to 31° in powder diffraction X-ray spectrum is at least 0.5 time the integral value of an independent peak present over an angle region of diffraction angle (2θ) of 21° to 22° of the spectrum.
9. A phosphor paste composition which comprises a phosphor dispersed in a solvent having a binder dissolved therein and wherein the phosphor is an alkaline earth aluminate phosphor as defined in claim 8 .
10. A vacuum ultraviolet excitation light emitting element which comprises a vacuum envelope having a fluorescent layer formed inside and a rare gas sealed in the vacuum envelope so that the fluorescent layer is excited by vacuum ultraviolet rays radiated by discharge of the rare gas, to emit light, and wherein a vacuum ultraviolet excitation alkaline earth aluminate phosphor as defined in claim 8 is used for the fluorescent layer.
11. A method of vacuum ultraviolet excitation comprising causing the alkaline earth aluminate phosphor according to claim 1 to emit light under excitation by vacuum ultraviolet rays having a wavelength of at most 200 nm.
12. A phosphor paste composition which comprises a phosphor dispersed in a solvent having a binder dissolved therein and wherein the phosphor is an alkaline earth aluminate phosphor as defined in claim 1 .
13. The phosphor paste composition according to claim 12 , wherein the content of the phosphor is from 5 to 70 wt %.
14. A vacuum ultraviolet excitation light emitting element which comprises a vacuum envelope having a fluorescent layer formed inside and a rare gas sealed in the vacuum envelope so that the fluorescent layer is excited by vacuum ultraviolet rays radiated by discharge of the rare gas, to emit light, and wherein a vacuum ultraviolet excitation alkaline earth aluminate phosphor as defined in claim 1 is used for the fluorescent layer.
15. The alkaline earth aluminate phosphor according to claim 1 , wherein 0.03≦x≦0.5 and 1.1≦a≦1.5.
16. The alkaline earth aluminate phosphor according to claim 1 , wherein M is Ba.
17. The alkaline earth aluminate phosphor according to claim 16 , wherein Ba is substituted in an amount of at most 50 mol % by at least one of Sr and Ca.
18. The alkaline earth aluminate phosphor according to claim 17 , wherein said amount is at most 20 mol %.
19. The alkaline earth aluminate phosphor according to claim 1 , wherein the half value width of the wide-band peak is at least 1.0°.
20. A method of preparing the alkaline earth aluminate phosphor according to claim 1 , which comprises baking starting material compounds of said phosphor at least once in a reducing atmosphere at a temperature of from 1300 to 1800° C.