Production method of lithium secondary battery and production device therefor
View Patent ↗A manufacturing method of the present invention includes ejecting a melt 61 of a solid electrolyte onto at least one electrode plate selected from a positive electrode plate 20 and a negative electrode plate 30 , thereby depositing the melt 61 onto the at least one electrode plate, and compressing the positive electrode plate 20 and the negative electrode plate 30 while sandwiching the melt 61 , thereby forming a layered body including the positive electrode plate 20 , an electrolyte layer 62 including the solid electrolyte, and the negative electrode plate 30 . In accordance with this manufacturing method, a thin lithium secondary battery having excellent characteristics can be manufactured in a highly productive manner.
1. A method for manufacturing a lithium secondary battery comprising a positive electrode plate, a negative electrode plate, and a solid electrolyte arranged between the positive electrode plate and the negative electrode plate; the method comprising:
(i) spraying a melt of the solid electrolyte from a sprayer onto at least one electrode plate selected from the positive electrode plate and the negative electrode plate, thereby depositing a sprayed layer of the melt onto the at least one electrode plate; and
(ii) compressing the positive electrode plate and the negative electrode plate while sandwiching the melt, thereby forming a layered body comprising the positive electrode plate, an electrolyte layer comprising the solid electrolyte, and the negative electrode plate.
2. The method according to claim 1 , wherein the solid electrolyte comprises Li 3 PO 4 .
3. The method according to claim 1 , wherein the solid electrolyte is Li 3 PO 4 , a solid electrolyte obtained by adding nitrogen to Li 3 PO 4 , or Li 3 PO 4 —Li 2 S—SiS 2 :
4. The method according to claim 1 , further comprising after the (ii) compressing,
(iii) layering the layered body by spraying the melt of the solid electrolyte onto at least one surface of the layered body and then winding the layered body.
5. The method according to claim 1 , wherein in the (ii) compressing, the layered body is formed by compressing the positive electrode plate and the negative electrode plate while cooling them down.
6. The method according to claim 1 . wherein the electrolyte layer has a thickness ranging from 0.1 μm to 10 μm.