Method of locally repairing parts covered with a thermal barrier
View Patent ↗A method of locally repairing parts coated with a thermal barrier including a ceramic outer layer and a metal underlayer of alumina-forming alloy for protecting the substrate against oxidation and for bonding with the ceramic outer layer, includes: defining the zone for repair with a mechanical mask adapted to the shape of the part and the zone for repair; scouring the zone for repair so as to remove the ceramic, the alumina layer, and the damaged portions of the underlayer; supplying materials for repairing the underlayer to the repair zone by subjecting the partially-scoured part to metal deposition by use of an electrical current; and subjecting the part to a heat treatment in order to enable the added metals to diffuse into the remaining underlayer in the repair zone for repair and to enable a surface film of alumina to form. After the underlayer has been reconstituted, the zone for repair is again defined by a mechanical mask and a new ceramic layer is deposited thereon.
1. A method of locally repairing parts coated with a thermal barrier comprising a ceramic outer layer and a metal underlayer of alumina-forming alloy for protecting a substrate against oxidation and for bonding with the ceramic outer layer, the method comprising:
defining the zone for repair with a first mechanical mask adapted to the shape of the part and the zone for repair;
scouring the zone for repair so as to remove from said zone the ceramic, the alumina layer, and the damaged portions of the underlayer;
supplying materials for repairing the underlayer to said zone by subjecting the partially-scoured part to metal deposition by an electrical current; and
subjecting the part to heat treatment in order to enable the deposited metals to diffuse into the remaining underlayer in the zone for repair and to enable a surface film of alumina to form.
2. A method according to claim 1 , wherein the zone for repair is scoured mechanically by sandblasting, sanding, grinding, or by laser beam.
3. A method according to claim 1 or claim 2 , wherein the materials for repairing the underlayer are supplied to the zone for repair by electrophoresis.
4. A method according to claim 1 , wherein platinum or palladium is deposited by electrolysis.
5. A method according to claim 1 , wherein a layer of aluminizing paint is applied on the deposited metals.
6. A method according to claim 1 , wherein, after subjecting the part to heat treatment, the zone for repair is again defined by a second mechanical mask and a new ceramic outer layer is deposited on the zone for repair.
7. A method according to claim 6 , wherein the new ceramic outer layer is deposited by a method of evaporating ceramic by electron bombardment.
8. A method according to claim 7 , wherein the surface of the zone for repair is exposed to a source for emitting ceramic vapor.
9. A method according to claim 8 , wherein the part is caused to pivot with oscillating motion of a given amplitude during exposure so as to deposit a substantially uniform layer of ceramic on the zone for repair.
10. A method according to claim 9 , wherein the part is caused to pivot with oscillating motion of a first amplitude in a first direction and a second amplitude in a second direction during exposure so as to deposit a substantially uniform layer of ceramic on the zone for repair.
11. A method according to claim 10 , wherein the first and second amplitudes are a function of an indentation made in the part during the scouring.
12. A method according to claim 9 , wherein the given amplitude is a function of an indentation made in the part during the scouring.
13. A method according to claim 1 , wherein the materials for repairing the underlayer are supplied to the zone of repair simultaneously by electrophoresis and by electrolysis.
14. A method according to claim 1 , wherein the zone for repair comprises flat side walls after the scouring.