MCrAlY-coating
View Patent ↗A gas turbine component consists of a superalloy base material with a single crystal structure and a protective MCrAlY-coating ( 6 ). The MCrAlY-coating ( 6 ) has a g/g′ single crystal structure, which is epitaxial with the base material. It has be determined the critical factors for the successful epitaxial and crack-free growth of the MCrAlY-coating ( 6 ).
1. An article having a surface and a single crystal structure, the article coated with protective MCrAlY-coating epitaxially grown on the surface of the article, wherein the MCrAlY-coating has a solidification temperature interval (ΔT 0 ) of smaller than 30° C. and a temperature interval (ΔT 1 ) of the last 5% liquid of smaller than 15° C., and wherein the MCrAlY has a γ/γ′-structure and the MCrAlY comprises less than 1.2 wt. % Si.
2. The article according to claim 1 , wherein the composition of the MCrAlY-coating is close to the eutectic line on the γ-phase side of the eutectic line of the ternary phase diagram of Ni—Al—Cr.
3. The article according to claim 1 , wherein the MCrAlY-coating comprises the following composition (wt. %): 18–26.0% Cr, 5–8.0% Al, 0.1–1.2% Si, 0.4–1.2% Y, 0–0.1% Hf, 0.1–1.2% Ta, balance Ni and unavoidable impurities, with Σ(Al+Si)<10%, Σ(Si+Ta)<2.5%, Σ(Y+Hf+Zr+La)<1.5%, C max. 0.03%.
4. The article according to claim 1 , wherein the MCrAlY-coating comprises (wt. %): Si up to 0.5%, Hf up to 0.5%, Y<0.5% and Ta<3%, individually or a combination thereof.
5. The article according to claim 1 , wherein the MCrAlY-coating comprises an addition of Fe, Ga, Mg, Ca, individually or a combination thereof.
6. The article according to claim 1 , wherein the MCrAlY-coating has a thickness of 100–300 μm.
7. The article according to claim 1 , wherein the MCrAlY-coating is applied by laser cladding.
8. The article according to claim 1 , which is a gas turbine component made from nickel base super alloy.
9. An article having a surface and a single crystal structure, the article coated with protective MCrAlY-coating epitaxially grown on the surface of the article, wherein the MCrAlY has a γ/γ′-structure and has the following chemical composition (wt. %): 25 Cr, 6 Al, 0.4 Y, less than 1.2 wt. % Si, balance Ni and unavoidable impurities.
10. The article according to claim 9 , wherein the MCrAlY-coating has a solidification temperature interval (ΔT 0 ) of 25° C.
11. The article according to claim 9 , which is a gas turbine component made from nickel base super alloy.
12. An article having a surface and a single crystal structure, the article coated with protective MCrAlY-coating epitaxially grown on the surface of the article, wherein the MCrAlY has a γ/γ′-structure and has the following chemical composition (wt. %): 16.5 Cr, 5.5 Al, 0.4 Y, less than 1.2 wt. % Si, balance Ni and unavoidable impurities.
13. The article according to claim 12 , wherein the MCrAlY-coating has a solidification temperature interval (ΔT 0 ) of 25° C.
14. The article according to claim 12 , which is a gas turbine component made from nickel base super alloy.