Physical blends of polyethylenes

1. A process for the preparation of a polyethylene resin composition having a narrow molecular weight distribution comprising:

a. providing a first metallocene-produced linear low density polyethylene (mLLDPE) resin having a density within the range of 0.92 to 0.94 g/cm 3 and a melt index MI2 within the range of 0.05 to 2 g/10 min.;

b. providing a second high density polyethylene (HDPE) resin prepared either with a Ziegler-Natta catalyst or with a metallocene catalyst and having a density within the range of 0.95 to 0.97 g/cm 3 and a melt index MI2 within the range of 0.1 to 10 g/10 min.; and

c. blending together said first and second polyethylenes to form a polyethylene resin composition having a narrow molecular weight distribution, a density within the range of 0.93 to 0.955 g/cm 3 and a melt index MI2 within the range of 0.5 to 8 g/10 min.

2. The process according to claim 1 wherein said blended polyethylene resin composition has a density within the range of 0.94 to 0.955.

3. The process according to claim 2 wherein said blended polyethylene resin composition has a melt index MI2 within the range of 0.5 to 3 g/10 min.

4. The process according to claim 1 wherein the first metallocene-produced linear low density polyethylene has a density of no more than 0.935 g/cm 3 .

5. The process according to claim 1 wherein the polyethylene resin composition is a physical blend and comprises at least 15 wt. % of the first metallocene-produced linear low density polyethylene.

6. The process according to claim 1 wherein the polyethylene resin composition is a physical blend and comprises from 20 to 80 wt. % of the first metallocene-produced linear low density polyethylene and from 80 to 20 wt. % of the second high density HDPE resin.

7. The process according to claim 1 wherein said blended polyethylene resin composition comprises from 30 to 50 wt. % of said linear low density polyethylene resin and from 50 to 70 wt. % of said second high density polyethylene.

8. The process according to claim 7 wherein said polyethylene resin composition has a density within the range of 0.94 to 0.955 g/cm 3 .

9. The process according to claim 8 wherein said polyethylene resin composition has a melt index MI2 within the range of 0.5 to 3 g/10 min.

10. The process according to claim 1 wherein said linear low density polyethylene resin and said high density polyethylene resin are produced in separate reactors, recovered from said separate reactors, and then physically blended together to produce said polyethylene resin composition.

11. The process according to claim 10 wherein said high density polyethylene resin is prepared with a Ziegler-Natta catalyst and the blend of said first and second polyethylenes has a narrower molecular weight distribution than the molecular weight distribution of said second high density polyethylene.

12. A process for the preparation of a polyethylene composition having a narrow molecular weight distribution which comprises:

a. contacting an ethylene monomer and a co-monomer comprising an alpha olefin having from 3 to 10 carbon atoms with a first catalyst system in a first reactor under first polymerization conditions to produce a first polyethylene resin having a first molecular weight, a first melt index MI2 of no more than 2 g/10 min. and a first density of no more than 0.94 g/cm 3 , said first catalyst system comprising (a) a metallocene catalyst comprising a bis tetrahydroindenyl compound or a bis(n-butyl-cyclopentadienyl) compound; and (b) a catalyst which activates the catalyst component;

b. providing a second polyethylene resin having a second density greater than said first density and a second melt index MI2 greater than said first melt index MI2 of said first polyethylene resin and prepared with a Ziegler-Natta or a metallocene catalyst; and

c. blending together the first and second polyethylene resins to form a polyethylene composition having a narrow molecular weight distribution, a melt index MI2 within the range of 0.5 to 3 g/10 min. and a density within the range of 0.94 to 0.955 g/cm 3 .

13. A process according to claim 11 wherein the metallocene catalyst used to prepare the first polyethylene resin is ethylene bis(4,5,6,7-tetrahydro-1-indenyl)zirconium dichloride.

14. A polyethylene resin composition having a narrow molecular weight distribution comprising:

a. a first metallocene-produced linear low density polyethylene (mLLDPE) resin having a density within the range of 0.92 to 0.94 g/cm 3 and a melt index MI2 within the range of 0.05 to 2 g/10 min.;

b. a second high density polyethylene (HDPE) resin prepared either with a Ziegler-Natta catalyst or with a metallocene catalyst and having a density within the range of 0.95 to 0.97 g/cm 3 and a melt index MI2 within the range of 0.1 to 10 g/10 min.; and

c. said first and second polyethylene resins being blended together to form a polyethylene resin composition having a narrow molecular weight distribution, a density within the range of 0.93 to 0.955 g/cm 3 and a melt index MI2 within the range of 0.5 to 8 g/10 min.

15. A container comprising a wall structure formed by a polyethylene composition according to claim 14 .

16. The container of claim 15 wherein said container is a fuel tank formed by injection molding.

17. The container of claim 15 wherein said container comprises a milk bottle formed by blow molding.

18. The system of claim 15 wherein said container is a container suitable for the packaging of cosmetic or pharmaceutical materials.