Process to reduce the temperature of a hydrogen and carbon monoxide containing gas and heat exchanger for use in said process
View Patent ↗A process to reduce the temperature of a hydrogen and carbon monoxide containing gas by contacting the gas with a metal alloy surface having a lower temperature than the temperature of the gas, wherein the metal alloy surface has between 0 and 20 wt % iron, between 0 and 5 wt % aluminium, between 0 and 5 wt % silicon, between 20 and 50 wt % chromium and at least 35 wt % nickel, wherein the metal alloy surface maintains it lower temperature than the temperature of the gas by making use of coolant water.
1. A process to reduce the formation of coke and to reduce the temperature of a hydrogen and carbon monoxide containing gas obtained from the partial oxidation of a hydrocarbon feedstock by contacting the gas with a metal alloy surface having a lower temperature than the temperature of the gas, wherein the metal alloy surface comprises between 0 and 20 wt % iron, between 1 and 5 wt % aluminium, between 0 and 5 wt % silicon, more than 30 wt % chromium and at least 35 wt % nickel, wherein said alloy metal surface is maintained at a lower temperature than the temperature of the gas by making use of coolant water, and whereby coke formation on the metal alloy surface is minimized.
2. The process of claim 1 , wherein the metal alloy surface comprises between 1 and 5 wt % silicon.
3. The process of claim 2 , wherein the metal alloy surface comprises between 0 and 2 wt % titanium and/or REM.
4. The process of claim 3 , wherein the metal alloy surface is supported with a metal alloy support layer having better mechanical properties than said surface layer.
5. The process of claim 4 , wherein the metal alloy support layer comprises between 7 and 98 wt % iron.
6. The process of claim 5 , wherein the metal alloy surface layer is applied to the metal alloy support layer by means of a build-up welding method.
7. The process of claim 6 , wherein the temperature of the hydrogen and carbon monoxide containing gas is reduced from a temperature of between 1000 and 1500° C. to a temperature between 300 and 750° C.
8. The process of claim 7 , wherein the hydrogen and carbon monoxide containing gas has a hydrogen to CO ratio of between 1.6 and 2.5.
9. The process of claim 8 , wherein the gas comprises less than 15 vol % steam.
10. The process of claim 9 , wherein the hydrocarbon feedstock to the partial oxidation process used to obtain the hydrogen and carbon monoxide containing gas is natural gas.
11. The process of claim 10 , wherein the gas is cooled by passing the gas through one or more conduits, which conduits are submerged in coolant water as contained in a vessel in which vessel steam is formed and discharged from said vessel and wherein the interior of the tubes consists of the metal alloy surface layer and the exterior of the tubes consist of the metal alloy support layer.
12. The process of claim 1 wherein the metal alloy surface has a thickness of from 1 to 5 mm and has an iron content less than 7 wt %.
13. The process of claim of claim 2 , wherein the hydrogen and carbon monoxide containing gas contains less than 30 vol % steam.
14. The process of claim 12 wherein the metal alloy surface layer has a thickness of from 1 to 3 mm and an iron content of less than 4 wt %.
15. A process to reduce the temperature of a hydrogen and carbon monoxide containing gas by contacting the gas with a metal alloy surface having a lower temperature than the temperature of the gas, wherein the metal alloy surface comprises between 0 and 20 wt % iron, between 1 and 5 wt % aluminium, between 1 and 5 wt % silicon, more than 30 wt % chromium and at least 35 wt % nickel, wherein said alloy metal surface is maintained at a lower temperature than the temperature of the gas by making use of coolant water.