Flame-retardant compositions of methanephosphonic acid, boric acid and an organic base
View Patent ↗Compositions are described that are obtainable by preparing a mixture of methanephosphonic acid, boric acid, water and optionally urea and subsequently adding dicyandiamide and/or guanylurea to this mixture. The compositions thus obtained are useful for conferring a flame-retardant finish on fibrous materials, especially on woven fabrics composed of cellulosic fibers.
1. A composition obtained by the following successive steps of:
a) preparing a mixture A), which includes methanephosphonic acid, boric acid and water,
b) adding dicyandiamide and/or guanylurea to said mixture A),
c) optionally neutralizing the resultant mix with a base.
2. A composition as claimed in claim 1 , wherein said mixture A) is heated to a temperature in the range from 70° C. to 95° C. after said step a) has been carried out and wherein step b) is carried out in said range from 70° C. to 95° C.
3. A composition as claimed in claim 1 , wherein said methanephosphonic acid used in said step a) was prepared by hydrolysis of mono- and/or dimethyl methanephosphonate.
4. A composition as claimed in claim 1 , wherein said mixture A) includes 25 to 50 parts by weight of methanephosphonic acid per 100 parts by weight of water and 0.1 mol to 0.3 mol of boric acid per mole of methanephosphonic acid.
5. A composition as claimed in claim 1 , wherein no guanylurea is used in said step b) and wherein 20 to 30 g of dicyandiamide are used per 100 g of said mixture A).
6. A composition as claimed in claim 1 , wherein said mixture A) additionally includes urea.
7. A composition as claimed in claim 6 , wherein said mixture A) includes 2 to 10 g of urea per 100 g of methanephosphonic acid.
8. A method of treating fibrous materials which comprises applying a composition as claimed in claim 1 thereto.
9. The method as claimed in claim 8 , wherein said fibrous materials are wovens which are 50 to 100% by weight cellulosic fiber.
10. The method as claimed in claim 8 , wherein said fibrous materials are textile fabrics.