Method of making models
View Patent ↗A method of a seamless model free of bond lines. The method includes the sequential steps of providing a substructure having an exposed outer surface, applying a modelling paste to a structure support in the form of a continuous layer, curing the applied modelling paste, and machining the cured layer of modelling paste to the desired contour. The modelling paste a low density curable composition prepared from thixotropic epoxy or polyurethane containing microballoons.
1. A method of making a seamless model comprising the steps of:
a) providing at least one tank filled with a resin component and tank filled with a hardener component;
b) delivering the resin component and hardener component from the tanks to a mix block and mixing the resin component and hardener component to produce a modeling paste wherein the modeling paste is a low density thixotropic curable paste comprising a resin composition and microballoons;
c) dispensing the modeling paste onto an outer surface of a support in a continuous layer;
d) curing the paste at room temperature; and
e) machining the cured paste to a desired or pre-determined contour to form the seamless model
wherein the microballoons are present in an amount of greater than about 50% and less than about 80% of the uncured paste by volume and wherein the density of the uncured paste is in the range of about 0.4 to about 0.9 g/cm 3 and
wherein the resin composition comprises:
(i) an epoxy resin;
(ii) a thixotropic agent; and
(iii) a hardener comprising at least one polyethyleneimine and at least one other amine having at least two hydrogen groups.
2. The method of claim 1 wherein the thixotropic agent is selected from the group consisting of: a hydrogen-bonding type of thixotropic agent present in an amount of about 0.2 to about 4% by weight of the paste; and a chemical thixotropic agent present in an amount of about 0.05 to about 1.5% by weight of the paste.
3. The method of claim 1 wherein the paste includes a filler in an amount of about 1% to about 30% by weight based on the weight of the paste.
4. The method of claim 1 wherein the thixotropic agent comprises a hydrophilic fumed silica and is present in an amount of about 1% to about 20% by weight based on the weight of the epoxy resin.
5. The method of claim 1 wherein the polyethyleneimine has a molecular weight of about 700 to about 1,000,000 and is present in an amount of about 0.2-2 parts by weight per 100 parts by weight of the epoxy resin.
6. The method of claim 5 wherein the other amine is an aliphatic amine comprising an N-hydroxyalkyl derivative of a polyalkylene polyamine and a polyaminoamide reaction product of a polyalkylenepolyamine and a polymerized vegetable oil acid.
7. The method of claim 1 wherein the resin composition further comprises ethylenically unsaturated component.
8. The method of claim 1 wherein the paste further comprises at least one molecular sieve, surfactant, antifoaming agent and calcium stearate.