Process for producing polyolefin membrane with integrally asymmetrical structure
View Patent ↗Process for producing an integrally asymmetrical hydrophobic polyolefinic membrane with a sponge-like, open-pored, microporous support structure and a separation layer with a denser structure, using a thermally induced liquid-liquid phase separation process. A solution of at least one polyolefin is extruded to form a shaped object. The solvent used is one for which the demixing temperature of a solution of 25% by weight of the polyolefin in this solvent is 10 to 70° C. above the solidification temperature. After leaving the die, the shaped object is cooled using a liquid cooling medium that does not dissolve the polymer up to the die temperature, until the phase separation and solidification of the high-polymer-content phase take place. The integrally asymmetrical membrane producible in this manner has a porosity of greater than 30% to 75% by volume, a sponge-like, open-pored, microporous support layer without macrovoids and with on average isotropic pores, and on at least one of its surfaces a separation layer with pores <100 nm, if any. The membrane is preferably used for gas separation or gas transfer processes, in particular for oxygenation of blood.
1. Process for producing an integrally asymmetrical hydrophobic membrane consisting of at least one polyolefin, the membrane having a sponge-like, open-pored, microporous support structure and a separation layer with a denser structure compared to the support structure, the process comprising at least the steps of:
a) preparing a homogeneous solution from a system comprising 20-90% by weight of the at least one polyolefin and 80-10% by weight of a solvent for the at least one polyolefin, wherein the system at elevated temperatures has a range in which it is present as a homogeneous solution, on cooling has a critical demixing temperature, below the critical demixing temperature in the liquid state of aggregation has a miscibility gap, and has a solidification temperature,
b) rendering the solution to form a shaped object, with first and second surfaces, in a die at a die temperature above the critical demixing temperature,
c) cooling the shaped object by contacting the shaped object with a liquid cooling medium that does not dissolve or react chemically with the at least one polyolefin at temperatures up to the die temperature, the liquid cooling medium being conditioned to a cooling temperature below the solidification temperature, at such a rate that a thermodynamic non-equilibrium liquid-liquid phase separation into a high-polymer-content phase and a low-polymer-content phase takes place and solidification of the high-polymer-content phase subsequently occurs when the temperature of the shaped object falls below the solidification temperature, and
d) optionally removing the low-polymer-content phase from the shaped object, wherein a solvent for the at least one polyolefin is selected for which, on cooling at a rate of 1° C./min, the demixing temperature of a solution of 25% by weight of the at least one polyolefin in the solvent is 10 to 70° C. above the solidification temperature.
2. Process for producing a membrane according to claim 1 , wherein the solvent for the at least one polyolefin is one for which, for a solution of 25% by weight of the at least one polyolefin in the solvent and a cooling rate of 1° C./min, the critical demixing temperature is 20 to 50° C. above the solidification temperature.
3. Process for producing a membrane according to claim 1 , wherein the solvent for the at least one polymer is one for which, for a solution of 25% by weight of the at least one polyolefin in the solvent and a cooling rate of 1° C./min, the critical demixing temperature is 25 to 45° C. above the solidification temperature.
4. Process for producing a membrane according to claim 1 , wherein the at least one polyolefin has a density of ≦910 kg/m 3 .
5. Process for producing a membrane according to claim 1 , wherein the liquid cooling medium is a non-solvent for the at least one polyolefin that, on heating up to a boiling point of the non-solvent, does not dissolve the at least one polyolefin to form a homogeneous solution.
6. Process for producing a membrane according to claim 1 , wherein the liquid cooling medium is a liquid that is a strong non-solvent for the at least one polyolefin and is homogeneously miscible with the solvent at the cooling temperature.
7. Process for producing a membrane according to claim 1 , wherein the liquid cooling medium has a temperature that is at least 100° C. below the critical demixing temperature.
8. Process for producing a membrane according to claim 1 , wherein 30-60% by weight of the at least one polyolefin is dissolved in 70-40% by weight of the solvent.
9. Process for producing a membrane according to claim 1 , wherein the at least one polyolefin consists exclusively of carbon and hydrogen.
10. Process for producing a membrane according to claim 9 , wherein the at least one polyolefin is a poly(4-methyl-1-pentene).
11. Process for producing a membrane according to claim 9 , wherein the at least one polyolefin is a polypropylene.
12. Process for producing a membrane according to claim 9 , wherein the at least one polyolefin is a mixture of a poly(4-methyl-1-pentene) and a polypropylene.
13. Process for producing a membrane according to claim 10 , wherein the solvent is palm nut oil, dibutyl phthalate, dioctyl phthalate, dibenzyl ether, coconut oil, or a mixture thereof.
14. Process for producing a membrane according to claim 11 , wherein the solvent is N,N-bis(2-hydroxyethyl)tallow amine, dioctyl phthalate, or a mixture thereof.
15. Process for producing a membrane according to claim 1 , wherein the membrane is a hollow-fiber membrane.