Case hardening bearing steel having excellent toughness and rolling contact fatigue life in intermediate temperature
View Patent ↗A case hardening bearing steel having an excellent rolling contact fatigue life in intermediate temperature, in addition, excellent toughness at room temperature is provided. Specific means for solving the problems are as follows. The composition contains, by mass percent, C of 0.15 to 0.30 mass percent, Si of 0.5 to 2.0 mass percent, Mn of 0.3 to 2.0 mass percent, Cr of 1.3 to 2.5 mass percent, Mo of 0.3 to 1.0 mass percent, and O of not more than 0.0012 mass percent in a range where (Si+Mo)≧1.0 mass percent is satisfied, and contains iron and inevitable impurities as remnant; the maximum size of oxide nonmetallic inclusion is not more than 12.5 μm when examined area is 320 mm 2 ; number of the oxide nonmetallic inclusion having a diameter of equivalent circle of 3 μm or more is not more than 250 when the examined area is 320 mm 2 ; in addition, C density of an outer layer is adjusted to be in a range from 0.7 to 1.2 mass percent by carburization.
1. A case hardening bearing steel having excellent toughness and an excellent rolling contact fatigue life in intermediate temperature comprising:
C of 0.15 to 0.30 mass percent,
Si of 0.5 to 2.0 mass percent,
Mn of 0.3 to 2.0 mass percent,
Cr of 1.75 to 2.5 mass percent,
Mo of 0.3 to 1.0 mass percent,
and O of not more than 0.0012 mass percent,
in a range where (Si+Mo)≧1.0 mass percent is satisfied, and containing iron and inevitable impurities as remnants; the maximum size of oxide nonmetallic inclusions is not more than 12.5 μm when an examined area is 320 mm 2 ; the number of the oxide nonmetallic inclusions having a diameter of equivalent circle of 3 μm or more is not more than 250 when the examined area is 320 mm 2 ; and a C density of an outer layer is adjusted in a range from 0.7 to 1.2 mass percent by carburization.
2. A ease hardening bearing steel having excellent toughness and an excellent rolling contact fatigue life in intermediate temperature comprising:
C of 0.15 to 0.30 mass percent,
Si of 0.5 to 2.0 mass percent,
Mn of 0.3 to 2.0 mass percent,
Cr of 1.75 to 2.5 mass percent,
Mo of 0.3 to 1.0 mass percent,
and O of not more than 0.00 12 mass percent,
and containing iron and inevitable impurities as remnants;
where (Si+Mo)≧1.0 mass percent is satisfied, the maximum size of oxide nonmetallic inclusions is not more than 12.5 μm when an examined area is 320 mm 2 , the number of the oxide non-metallic inclusions having a diameter of equivalent circle of 3 μm or more is not more than 250 when the examined area is 320 mm 2 , and a C density to a depth of 0.5 mm of an outer layer is adjusted in a range from 0.7 to 1.2 mass percent by carburization.
3. A case hardening bearing steel having excellent toughness and an excellent rolling contact fatigue life in intermediate temperature consisting essentially of,
C of 0.15 to 0.30 mass percent,
Si of 0.5 to 2.0 mass percent,
Mn of 0.3 to 2.0 mass percent,
Cr of 1.75 to 2.5 mass percent,
Mo of 0.3 to 1.0 mass percent,
and O of not more than 0.00 12 mass percent,
in a range where (Si+Mo)≧1.0 mass percent is satisfied, and containing iron and inevitable impurities as remnants; the maximum size of oxide nonmetallic inclusions is not more than 12.5 μm when an examined area is 320 mm 2 ; the number of the oxide nonmetallic inclusions having a diameter of equivalent circle of 3 μm or more is not more than 250 when the examined area is 320 mm 2 ; and a C density of an outer layer is adjusted in a range from 0.7 to 1.2 mass percent by carburization.
4. A case hardening bearing steel having excellent toughness and an excellent rolling contact fatigue life in intermediate temperature consisting essentially of,
C of 0.15 to 0.30 mass percent,
Si of 0.5 to 2.0 mass percent,
Mn of 0.3 to 2.0 mass percent,
Cr of 1.75 to 2.5 mass percent,
Mo of 0.3 to 1.0 mass percent,
and O of not more than 0.0012 mass percent,
and containing iron and inevitable impurities as remnants;
where (Si+Mo)≧1.0 mass percent is satisfied, the maximum size of oxide nonmetallic inclusions is not more than 12.5 μm when an examined area is 320 mm 2 ,the number of the oxide non-metallic inclusions having a diameter of equivalent circle of 3 μm or more is not more than 250 when the examined area is 320 mm 2 , and a C density to a depth of 0.5 mm of an outer layer is adjusted in a range from 0.7 to 1.2 mass percent by carburization.