Method for manufacturing core material for electrode plate and method for manufacturing alkaline storage battery
View Patent ↗A plate core material is manufactured by a method including the processes of soaking a core material ( 11 ) that is made of nickel or nickel-plated steel and includes copper as an impurity in an aqueous solution ( 12 ) containing ammonium ions and hydrogen peroxide, so that the copper is dissolved in the aqueous solution ( 12 ), and removing the aqueous solution ( 12 ) from the surface of the core material ( 11 ). Further, an alkaline storage battery is manufactured by a method including this manufacturing method. According to the manufacturing method of the present invention, an alkaline storage battery having higher reliability than that of a conventional alkaline storage battery can be obtained.
1. A method for manufacturing an alkaline storage battery having a positive electrode including a core material and an active material carried by the core material, comprising:
manufacturing the core material using a method for manufacturing a plate core material of an alkaline storage battery that is made of nickel or nickel-plated steel, comprising:
(i) bringing a core material that is made of nickel or nickel-plated steel and includes copper as an impurity into contact with an aqueous solution containing ammonium ions and hydrogen peroxide, so that the copper is dissolved in the aqueous solution; and
(ii) removing the aqueous solution from a surface of the core material to provide the plate core material of nickel or nickel-plated steel.
2. The method for manufacturing an alkaline storage battery according to claim 1 , further comprising assembling the core material into an alkaline storage battery.
3. The method for manufacturing an alkaline storage battery according to claim 1 , wherein the core material is soaked in the aqueous solution in the process of (i).
4. The method for manufacturing an alkaline storage battery according to claim 1 , wherein at least one selected from the group consisting of ammonia, ammonium chloride, and ammonium acetate is dissolved in the aqueous solution.
5. The method for manufacturing an alkaline storage battery according to claim 1 , wherein a temperature of the aqueous solution is in a range of 10° C. to 30° C.
6. The method for manufacturing an alkaline storage battery according to claim 1 , wherein the core material is a nickel porous body including copper as an impurity.
7. The method for manufacturing an alkaline storage battery according to claim 1 , comprising, before the process of (i):
coiling the core material around a roller,
wherein in the process of (i), the core material is brought into contact with the aqueous solution by rotating the roller in a state where the roller is arranged such that a central axis of the roller is horizontal to a surface of the aqueous solution and a portion of the core material is soaked in the aqueous solution.
8. The method for manufacturing an alkaline storage battery according to claim 1 ,
wherein the core material is coiled, and
the process of (ii) includes:
(ii-1) washing the core material with a rinsing liquid;
(ii-2) removing the rinsing liquid from the surface of the core material by rotating the core material; and
(ii-3) drying the core material.