Interlayer composite structure for laminating glass with controlled diffusing properties at high transmission and a process for making same
View Patent ↗The present invention is a translucent interlayer, or a laminate obtained therefrom, that has low clarity, high haze, and light transmission of at least 60 percent wherein the aesthetic qualities of etched or sandblasted glass are substantially recreated. In addition, a laminate of the present invention provides the safety characteristics of laminated safety glass. In addition, the process for making the translucent laminates of the present invention can eliminate the safety and environmental concerns related to sandblasting or etching processes.
1. An interlayer composition comprising particles of colorant having a particle size of less than about 10 microns, wherein an interlayer sheet formed from the interlayer composition: (1) has a haze of from about 25 percent to about 90 percent, (2) allows at least about 60 percent of incident light to be transmitted through the interlayer, and (3) has clarity of at least 20%.
2. The composition of claim 1 wherein the colorant has a particle size of from about 2 microns to about 10 microns.
3. The composition of claim 2 wherein the colorant has a particle size of from about 2.5 microns to about 8 microns.
4. The composition of claim 3 wherein the colorant has a particle size of from about 3 microns to about 6 microns.
5. The composition of claim 1 wherein the concentration of the colorant is less about 2.0 weight percent based on the total weight of the interlayer.
6. The composition of claim 5 wherein the concentration of colorant is from about 0.9 weight percent to about 1.8 weight percent.
7. The composition of claim 6 wherein the concentration of colorant is from about 0.6 weight percent to about 1.5 weight percent.
8. The composition of claim 7 wherein the concentration of colorant is from about 0.3 weight percent to about 0.75 weight percent.
9. The composition of claim 8 wherein the colorant is selected from the group consisting of: BaSO 4 ; MgSiO 3 ; MgSO 4 ; MgO; ZnO; ZnSO 4 ; Sb x O y wherein x is either 2 or 4 and y is from 3 to 6; TiO 2 ; Ca 3 (PO 4 ) 2 ; CaSO 4 ; CaCO 3 , or any mixture thereof.
10. The composition of claim 9 wherein the colorant is selected from TiO 2 , CaCO 3 , or a mixture thereof.
11. The composition of claim 10 wherein the colorant is CaCO 3 .
12. A glass laminate comprising at least two pieces of glass and an interlayer composition positioned therebetween to form an interlaver sheet, wherein the interlayer sheet: (1) comprises particles of colorant having a particle size of less than about 10 microns, (2) has a haze of from about 25 percent to about 90 percent, (3) allows at least about 60 percent of incident light to be transmitted through the interlayer, and (4) has clarity of at least 20%.
13. The glass laminate of claim 12 wherein the interlayer composition comprises a colorant having a particle size of from about 2 microns to about 10 microns.
14. The glass laminate of claim 13 wherein the interlayer composition includes a colorant having a particle size of from about 2.5 microns to about 8 microns.
15. The glass laminate of claim 14 wherein the interlayer composition includes a colorant having a particle size of from about 3 microns to about 6 microns.
16. The glass laminate of claim 12 wherein the percent haze is from about 40 percent to about 85 percent.
17. The glass laminate of claim 16 wherein the percent haze is from about 50 percent to about 80 percent.
18. The glass laminate of claim 17 wherein the percent haze is from about 55 percent to about 75 percent.
19. The glass laminate of claim 12 which transmits from at least about 75 percent of incident light.
20. The glass laminate of claim 19 which transmits at least about 80 percent of the incident light.
21. The glass laminate of claim 20 which transmits at least about 85 percent of the incident light.
22. The glass laminate of claim 12 wherein the clarity is from about 35% to about 100%.
23. The glass laminate of claim 22 wherein the clarity is from about 45% to about 95%.
24. The glass laminate of claim 23 wherein the clarity is from about 50% to about 90%.
25. The glass laminate of claim 24 wherein the clarity is from about 60% to about 85%.
26. A process for producing an PVB sheet suitable for laminated glass applications, the process comprising the steps of (a) feeding colorant into an extruder at a controlled rate; (b) co-extruding polyvinyl butyral resin, colorant, plasticizer, and other optional additives; (c) quenching the molten sheet composition to obtain a PVB sheet having dimensional stability suitable for laminated glass applications, wherein the PVB sheet: (1) has a haze of from about 25 percent to about 90 percent, (2) allows at least about 60 percent of incident light to be transmitted through the interlayer, and (3) has clarity of at least 20%.