Removal of arsenic from drinking and process water
View Patent ↗A method of removing arsenic and heavy metals from water using metal salt hydroxidegels is provided. The arsenic present in water is adsorbed onto the hydroxide-gels which can effectively be filtered through a diatomaceous earth (DE) filtration bed. The combination of DE mixed hydroxide-gels is also effective in removing arsenic from water and heavy metals from water.
1. A method of removing arsenic from arsenic-containing water comprising: coating diatomaceous earth with one or more metal salt hydroxide-gels to form diatomaceous earth pre-coated hydroxide-gels, wherein said metal salt is selected from the group consisting of lanthanum salt, ferric salt, and aluminum salt; contacting said arsenic-containing water with said diatomaceous earth pre-coated hydroxide-gels; and filtering said water through a diatomaceous earth filter bed or a diatomaceous earth-precoat filter.
2. The method of claim 1 , wherein said said filtering uses a filter screen or septum made of water-compatible material coated with diatomaceous earth.
3. The method of claim 2 , wherein said water-compatible material is polyethylene, polypropylene or stainless steel.
4. The method of claim 1 , wherein said filter is a diatomaceous earth filter bed.
5. The method of claim 1 , wherein said metal salt hydroxide-gel is formed by adjusting the pH of a solution containing metal salts so that a metal salt hydroxide-gel is formed.
6. The method of claim 1 , wherein diatomaceous earth pre-coated hydroxide-gels are contacted with said arsenic-containing water at a pH from about 2 to about 14.
7. The method of claim 1 wherein said contacting step is performed using a member of the group consisting of: mechanical mixing, ultrasonic mixing, mixing in-line using an atomizer, mixing in-line using venturi and mixing using metering pumps.
8. The method of claims 1 , wherein said metal salt hydroxide-gel is formed from at least one member of the group consisting of: lanthanum chloride, lanthanum nitrate, lanthanum carbonate, ferric chloride, ferric sulfate, aluminum chloride, aluminum nitrate, aluminum sulfate, and sodium aluminate.
9. The method of claim 8 , wherein said metal salt comprises more than one metal salt.
10. The method of claim 1 , wherein said arsenic-containing water contains arsenic at a concentration of about 10 ppb to 100 ppm.
11. The method of claim 10 , wherein said arsenic-containing water contains one or more members selected from the group consisting of: arsenite and arsenate.
12. The method of claim 10 , wherein said arsenic-containing water comprises one or more members of the group selected from: raw water, well water, drinking water, and process water.
13. The method of claim 1 , wherein said precoated hydroxide-gels are contacted with said arsenic-containing water for a time of between about 1 minute to about 6 minutes at a pH between about 3 and about 12.
14. The method of claim 1 , wherein said metal salt hydroxide-gel comprises lanthanum and ferric hydroxides.
15. The method of claim 1 , wherein metal salt hydroxide-gels comprise weight ratios of between about 1:1 and 1:10 of lanthanum: ferric hydroxides.
16. The method of claim 1 , wherein said metal salt hydroxide-gel consists essentially of lanthanum hydroxide.
17. The method of claim 1 , wherein said metal salt hydroxide-gel comprises a lanthanum hydroxide.