Process for producing modified polymer, modified polymer obtained by the process, and rubber composition
The present invention relates to a process for producing a modified polymer, comprising modifying a polymer having an active site of an organometal type in a molecule by reacting the site thereof with a hydrocarbyloxysilane compound and adding a condensation accelerator to the reaction system in the middle of the above reaction and/or after completion thereof and a rubber composition comprising the modified polymer obtained by the process described above, preferably a rubber composition comprising 100 parts by weight of (A) a rubber component containing at least 30% by weight of the above modified polymer and 10 to 100 parts by weight of (B) silica and/or carbon black.
1. A process for producing a modified polymer, comprising a first and second modification process,
the first modification process comprising modifying a polymer produced by anionic polymerization using an alkaline metal compound and/or an alkaline earth metal compound as a polymerization initiator and having an active site of an organometal in a molecule by reacting the site thereof with a hydrocarbyloxysilane compound, and
the second modification process comprising adding a condensation accelerator to the reaction system in the middle of the above reaction, or adding a condensation accelerator to the reaction system in the middle of the above reaction and after the completion thereof,
the condensation accelerator accelerates condensation of the modified polymer resulting in a condensed polymer,
the condensed polymer being recovered from the system,
wherein the polymer described above is a polymer obtained by homopolymerizing a conjugated diene compound or copolymerizing a conjugated diene compound with at least one additional monomer, and the hydrocarbyloxysilane compound described above used for the modification is at least one selected from a hydrocarbyloxysilane compound represented by Formula (I) and/or a partial condensation product thereof;
(wherein A 1 represents a monovalent group having at least one functional group selected from (thio)epoxy, (thio)isocyanate, (thio)ketone, (thio)aldehyde, imine, amide, trihydrocarbyl isocyanurate, (thio)carboxylates, metal salts of (thio)carboxylates, carboxylic anhydrides, carboxylic halides and dihydrocarbyl carbonate; R 1 represents a single bond or a divalent inactive hydrocarbon group; R 2 and R 3 each represent independently a monovalent aliphatic hydrocarbon group having 1 to 20 carbon atoms or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms; n is an integer of 0 to 2, and when a plurality of OR 3 is present, a plurality OR 3 may be the same as or different from each other; and an active proton and an onium salt are not contained in the molecule), and a hydrocarbyloxysilane compound represented by Formula (II) and/or a partial condensation product thereof;
(wherein A 2 represents a monovalent group having at least on functional group selected from cyclic tertiary amine, non-cyclic tertiary amine, nitrile, pyridine, sulfide and multisulfide; R 4 represents a single bond or a divalent inactive hydrocarbon group; R 5 and R 6 each represent independently a monovalent aliphatic hydrocarbon group having 1 to 20 carbon atoms or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms; m is an integer of 0 to 2, and when a plurality of OR 6 is present, a plurality OR 6 may be the same as or different from each other; and an active proton and an onium salt are not contained in the molecule).
2. The process for producing a modified polymer as described in claim 1 , wherein the metal in the active site is at least one selected from alkaline metals and alkaline earth metals.
3. The process for producing a modified polymer as described in claim 1 , wherein the at least one additional monomer is an aromatic vinyl compound.
4. The process for producing a modified polymer as described in claim 3 , wherein the aromatic vinyl compound is styrene.
5. The process for producing a modified polymer as described in claim 3 , wherein the active site is present at an end of the polymer, and at least a part thereof stays in an active state.
6. The process for producing a modified polymer as described in claim 1 , wherein the hydrocarbyloxysilane compound for modification is added to the polymer having an active site of an organometal in a molecule in a stoichiometric amount or an excess amount thereover based on the active site to react the active site with the hydrocarbyloxysilane compound.
7. The process for producing a modified polymer as described in claim 1 , wherein the condensation accelerator comprises combination of carboxylic acid salt of tin and/or titanium alkoxide with water.
8. The process for producing a modified polymer as described in claim 7 , wherein the carboxylic acid salt of tin is tin bis(2-ethylhexanoate) and the titanium alkoxide is titanium tetrakis(2-ethylhexyl oxide).
9. The process for producing a modified polymer as described in claim 7 , wherein the carboxylic acid salt of tin is a tin compound having an oxidation number of 2 represented by the following Formula (IV):
Sn(OCOR 9 ) 2 (IV)
(wherein R 9 is an alkyl group having 2 to 19 carbon atoms) or a tin compound having an oxidation number of 4 represented by the following Formula (V):
R 10 x SnA 3 y B 1 4−y−x (V)
(wherein R 10 is an aliphatic hydrocarbon group having 1 to 30 carbon atoms; x is an integer of 1 to 3; y is 1 or 2; A 3 is a group selected from a carboxyl group having 2 to 30 carbon atoms, an α,γ-dionyl group having 5 to 20 carbon atoms, a hydrocarbyloxy group having 3 to 20 carbon atoms and a siloxy group tri-substituted with a hydrocarbyl group having 1 to 20 carbon atoms and/or a hydrocarbyloxy group having 1 to 20 carbon atoms; and B 1 is a hydroxyl group or halogen), and the titanium alkoxide is a titanium compound by the following Formula (VI):
A 4 z TiB 2 4−z (VI)
(wherein A 4 is a group selected from an alkoxy group having 3 to 20 carbon atoms and a siloxy group tri-substituted with an alkyl group having 1 to 20 carbon atoms and/or an alkoxy group having 1 to 20 carbon atoms; B 2 is an α,γ-dionyl group having 5 to 20 carbon atoms; and z is 2 or 4).
10. The process for producing a modified polymer as described in claim 1 , wherein the conjugated diene compound is 1,3-butadiene or isoprene.
11. A modified polymer obtained by the production process as described in claim 1 , where the modified polymer is condensed at a modified moiety of said polymer.
12. The modified polymer as described in claim 11 , having a Mooney viscosity (ML 1+4 /100° C.) of 10 to 150.
13. A rubber composition comprising the modified polymer as described in claim 11 or 12 .
14. The rubber composition as described in claim 13 , comprising 100 parts by weight of (A) a rubber component containing at least 15% by weight of the modified polymer and 10 to 100 parts by weight of (B) an inorganic filler and/or carbon black.
15. The rubber composition as described in claim 14 , comprising 10 to 100 parts by weight of silica as the inorganic filler.
16. A tire using the rubber composition as described in claim 13 .
17. The modified polymer as described in claim 11 , having a weight average molecular weight (Mw) of 55.4×10 4 to 62.3×10 4 .
18. The process for producing a modified polymer as described in claim 1 , wherein the anionic polymerization is conducted in the presence of a randomizer.
19. A process for producing a modified polymer, comprising a first and second modification process,
the first modification process comprising modifying a polymer produced by anionic polymerization using an alkaline metal compound and/or an alkaline earth metal compound as a polymerization initiator and having an active site of an organometal in a molecule by reacting the site thereof with a hydrocarbyloxysilane compound, and
the second modification process comprising adding a condensation accelerator to the reaction system after the completion thereof,
the condensation accelerator accelerates condensation of the modified polymer resulting in a condensed polymer,
the condensed polymer being recovered from the system,
wherein the polymer described above is a polymer obtained by homopolymerizing a conjugated diene compound or copolymerizing a conjugated diene compound with at least one additional monomer, and the hydrocarbyloxysilane compound described above used for the modification is at least one selected from a hydrocarbyloxysilane compound represented by Formula (I) and/or a partial condensation product thereof;
(wherein A 1 represents a monovalent group having at least one functional group selected from (thio)epoxy, (thio)isocyanate, (thio)ketone, (thio)aldehyde, imine, amide, trihydrocarbyl isocyanurate, (thio)carboxylates, metal salts of (thio)carboxylates, carboxylic anhydrides, carboxylic halides and dihydrocarbyl carbonate; R 1 represents a single bond or a divalent inactive hydrocarbon group; R 2 and R 3 each represent independently a monovalent aliphatic hydrocarbon group having 1 to 20 carbon atoms or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms; n is an integer of 0 to 2, and when a plurality of OR 3 is present, a plurality OR 3 may be the same as or different from each other; and an active proton and an onium salt are not contained in the molecule), and a hydrocarbyloxysilane compound represented by Formula (II) and/or a partial condensation product thereof;
(wherein A 2 represents a monovalent group having at least on functional group selected from cyclic tertiary amine, non-cyclic tertiary amine, nitrile, pyridine, sulfide and multisulfide; R 4 represents a single bond or a divalent inactive hydrocarbon group; R 5 and R 6 each represent independently a monovalent aliphatic hydrocarbon group having 1 to 20 carbon atoms or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms; m is an integer of 0 to 2, and when a plurality of OR 6 is present, a plurality OR 6 may be the same as or different from each other; and an active proton and an onium salt are not contained in the molecule).
20. The process for producing a modified polymer as described in claim 19 , wherein the metal in the active site is at least one selected from alkaline metals and alkaline earth metals.
21. The process for producing a modified polymer as described in claim 19 , wherein the at least one additional monomer is an aromatic vinyl compound.
22. The process for producing a modified polymer as described in claim 21 , wherein the active site is present at an end of the polymer, and at least a part thereof stays in an active state.
23. The process for producing a modified polymer as described in claim 21 , wherein the aromatic vinyl compound is styrene.
24. The process for producing a modified polymer as described in claim 19 , wherein the hydrocarbyloxysilane compound for modification is added to the polymer having an active site of an organometal in a molecule in a stoichiometric amount or an excess amount thereover based on the active site to react the active site with the hydrocarbyloxysilane compound.
25. The process for producing a modified polymer as described in claim 19 , wherein the condensation accelerator comprises combination of carboxylic acid salt of tin and/or titanium alkoxide with water.
26. The process for producing a modified polymer as described in claim 25 , wherein the carboxylic acid salt of tin is a tin compound having an oxidation number of 2 represented by the following Formula (IV):
Sn(OCOR 9 ) 2 (IV)
(wherein R 9 is an alkyl group having 2 to 19 carbon atoms) or a tin compound having an oxidation number of 4 represented by the following Formula (V):
R 10 x SnA 3 y B 1 4−y−x (V)
(wherein R 10 is an aliphatic hydrocarbon group having 1 to 30 carbon atoms; x is an integer of 1 to 3; y is 1 or 2; A 3 is a group selected from a carboxyl group having 2 to 30 carbon atoms, an α,γ-dionyl group having 5 to 20 carbon atoms, a hydrocarbyloxy group having 3 to 20 carbon atoms and a siloxy group tri-substituted with a hydrocarbyl group having 1 to 20 carbon atoms and/or a hydrocarbyloxy group having 1 to 20 carbon atoms; and B 1 is a hydroxyl group or halogen), and the titanium alkoxide is a titanium compound by the following Formula (VI):
A 4 z TiB 2 4−z (VI)
(wherein A 4 is a group selected from an alkoxy group having 3 to 20 carbon atoms and a siloxy group tri-substituted with an alkyl group having 1 to 20 carbon atoms and/or an alkoxy group having 1 to 20 carbon atoms; B 2 is an α,γ-dionyl group having 5 to 20 carbon atoms; and z is 2 or 4).
27. The process for producing a modified polymer as described in claim 25 , wherein the carboxylic acid salt of tin is tin bis(2-ethylhexanoate) and the titanium alkoxide is titanium tetrakis(2-ethylhexyl oxide).
28. The process for producing a modified polymer as described in claim 19 , wherein the conjugated diene compound is 1,3-butadiene or isoprene.
29. A modified polymer obtained by the production process as described in claim 19 , where the modified polymer is condensed at a modified moiety of said polymer.
30. The modified polymer as described in claim 29 , having a Mooney viscosity (ML 1+4 /100° C.) of 10 to 150.
31. A rubber composition comprising the modified polymer as described in claim 29 or 30 .
32. The rubber composition as described in claim 31 , comprising 100 parts by weight of (A) a rubber component containing at least 15% by weight of the modified polymer and 10 to 100 parts by weight of (B) an inorganic filler and/or carbon black.
33. The rubber composition as described in claim 32 , comprising 10 to 100 parts by weight of silica as the inorganic filler.
34. A tire using the rubber composition as described in claim 31 .
35. The modified polymer as described in claim 29 , having a weight average molecular weight (Mw) of 55.4×10 4 to 62.3×10 4 .
36. The process for producing a modified polymer as described in claim 19 , wherein the anionic polymerization is conducted in the presence of a randomizer.