Solid electrolyte, photoelectric converter and process for producing the same
View Patent ↗The present invention relates to a solid electrolyte having superior conductive properties and reliability, a photovoltaic device using this electrolyte, and manufacturing methods thereof. The solid electrolyte of the present invention is a solid electrolyte having an electrolyte composition and a matrix polymer. The matrix polymer is formed by polymerization of a first compound having at least two isocyanate groups and a second compound having at least two nucleophilic groups containing active hydrogen in accordance with a polyaddition reaction, and the polymerization is performed after a precursor for the matrix polymer is brought into contact with a surface on which the solid electrolyte is to be formed.
1. A method of forming an electrolyte layer comprising an electrolyte composition and a matrix polymer, the method comprising:
forming the matrix polymer by polymerization of a first compound having at least three isocyanate groups and a second compound having at least two nucleophilic groups containing active hydrogen, wherein said polymerization is performed in accordance with a Michael addition reaction and wherein said polymerization is performed after a precursor for the matrix polymer is brought into contact with a surface on which the electrolyte is to be formed;
wherein the electrolyte layer is formed between two electrodes.
2. The method according to claim 1 , wherein the electrolyte composition comprises a solvent to form a gel electrolyte.
3. The method according to claim 1 , wherein the electrolyte composition comprises no solvent to form a solid electrolyte.
4. The method according to claim 1 , wherein the electrolyte composition comprises an ionic liquid to form a gel electrolyte.
5. The method according to claim 1 , wherein the electrolyte composition comprises a redox couple.
6. The method according to claim 5 , wherein the redox couple is a combination of a halogen ion and a halide ion.
7. The method according to claim 6 , wherein a halogen portion of the redox couple is iodine.
8. A photocell comprising: a semiconductor layer composed of semiconductor particles carrying a dye and an electrolyte layer, the layers being provided between a counter electrode and an electrode formed on a surface of a substrate;
wherein the electrolyte layer has a redox couple, an electrolyte composition, and a matrix polymer; and
wherein the matrix polymer is a polymer formed by polymerization of a first compound having at least three isocyanate groups and a second compound having at least two nucleophilic groups containing active hydrogen, wherein said polymerization is performed in accordance with a Michael addition reaction.
9. The photocell according to claim 8 , wherein the substrate is a transparent substrate.
10. A method for manufacturing a photocell comprising:
injecting a mixed solution between a counter electrode and an electrode formed on a surface of a substrate, the mixed solution containing a first compound having at least three isocyanate groups, a second compound having at least two nucleophilic groups containing active hydrogen, and an electrolyte composition having a redox couple; and
polymerizing, in accordance with a Michael addition reaction, the first compound and the second compound after the mixed solution is brought into contact with the electrode formed on the surface of the substrate.
11. The method for manufacturing a photocell, according to claim 10 , further comprising forming a semiconductor layer, composed of semiconductor particles carrying a dye, between the electrode and the counter electrode.
12. The method for manufacturing a photocell, according to claim 10 , wherein the electrolyte composition has a redox couple.
13. A method for manufacturing a photocell comprising:
forming a semiconductor layer composed of semiconductor particles carrying a dye between a counter electrode and an electrode formed on a surface of a substrate;
applying a first compound having at least three isocyanate groups and a second compound having at least two nucleophilic groups containing active hydrogen; and
polymerizing, in accordance with a Michael addition reaction, the first compound and the second compound.