Polyolefin films with improved processing properties
View Patent ↗The present invention relates to a process for reducing water carry-over during the production of polyolefin films or polyolefin tapes which are passed through a waterbath, where the polyolefin formulation comprises polyolefin waxes. The results are that less water is carried over and that the products have higher quality and better processing properties.
1. A process for reducing water carry-over during the production of a polyolefin film or polyolefin tape which is passed through a waterbath, comprising the step of providing a polyolefin formulation wherein the polyolefin formulation includes at least one polyolefin wax, wherein the at least one polyolefin wax has a weight-average molar mass Mw of from 4800 to 50 000 g/mol, and wherein the at least one polyolefin wax is incorporated into the polyolefin formulation.
2. The process according to claim 1 , wherein the at least one polyolefin wax is a polar or non-polar polyethylene wax or a polar or non-polar polypropylene wax.
3. The process according to claim 1 , wherein the at least one polyolefin wax is an unmodified or polar-modified wax with a number-average molar mass Mn of from 700 to 10 000 g/mol, with a drop point or softening point of from 70 to 170° C. measured by the ring/bore method, with a melt viscosity of from 5 to 50 000 mPa.s, measured at a temperature 10° C. above the drop point or softening point, with an acid value of from 0 to 100 mg KOH/g, and with a saponification value of from 0 to 150mg KOH/g.
4. The process according to claim 1 , wherein the at least one polyolefin wax is prepared by Ziegler-Natta or metallocene catalysts.
5. The process according to claim 1 , wherein the polyolefin wax is used at a concentration of from 0.01 to 3% by weight of the polyolefin formulation.
6. A polyolefin film or polyolefin tape made in accordance with the process of claim 1 .
7. A Polyolefin film or polyolefin tape with reduced water carry-over or passage through a waterbath, comprising a polyolefin formulation and wherein the polyolefin formulation includes at least one polar or non-polar polyethylene wax or polar or non-polar polypropylene wax, prepared by Ziegler-Natta or metallocene catalysts, wherein the at least one polar or non-polar polyethylene wax or polar or non-polar polypropylene wax, prepared by Ziegler-Natta or metallocene catalysts has a weight-average molar mass Mw of from 4800 to 50 000 g/mol, and wherein the at least one polar or non-polar polyethylene wax or polar or non-polar polypropylene wax, prepared by Ziegler-Natta or metallocene catalysts is incorporated into the polyolefin formulation.
8. A polyolefin film or polyolefin tape according to claim 7 , wherein the at least one one polar or non-polar polyethylene wax or polar or non-polar polypropylene wax, prepared by Ziegler-Natta or metallocene catalysts further comprises at least one unmodified or polar-modified wax with a number-average molar mass Mn of from 700 to 10 000 g/mol, with a drop point or softening point of from 70 to 170° C. measured by the ring/bore method, with a melt viscosity of from 5 to 50 000 mPa.s, measured at a temperature 10° C. above the drop point or softening point, with an acid value of from 0 to 100 mg KOH/g, and with a saponification value of from 0 to 150 mg KOH/g.
9. A polyolefin film or polyolefin tape according to claim 7 further comprising at least one pigment.