Method for producing a fully transposed high T
View Patent ↗A fully transposed composite superconductor of the Roebel bar type is produced. The superconductor is formed from combines superconductors. The process step for forming the subconductors, which are being configured with a lateral projection into a region of a neighbouring subconductor, is separated from the stranding step. Carrier strips, which are coated with the superconductive material, are used as the conductors.
1. A method for producing a fully transposed composite superconductor with an at least approximately rectangular cross section, comprising:
first producing a plurality of individual shaped and coated conductor elements, each having a ribbon shape with an approximately rectangular cross section corresponding to an individual shape of the conductor element in a transposed arrangement of the composite superconductor;
wherein
each shaped and coated conductor element has at least partially a coating of a superconductive high-T C material,
each shaped and coated conductor element satisfies the relationship B<H< 20 ·B, where B is a width of the shaped and coated conductor element and H is the length of an upright bending zone of the conductor element, in a current-carrying direction in the transposed arrangement, and
upright bending of the conductor elements in the coated state is avoided; and
after producing the individual shaped and coated conductor elements, assembling the shaped and coated conductor elements to said composite superconductor in the transposed arrangement by fitting the individual shaped and coated conductor elements with one another in a process separate from producing each conductor element, wherein
the conductor elements are shaped by cutting an initial body to a desired shape, and
the initial body is coated with the superconductive high-T C material before the conductor elements are cut therefrom, to the desired shape.
2. The method as claimed in claim 1 , wherein
each conductor element is formed from a supporting ribbon coated with the superconductive high-T C material, and
the supporting ribbon is formed from a steel alloy or a nickel alloy.
3. The method as claimed in claim 1 , wherein the conductor elements are fixed to one another by adhesive bonding or soldering joints in the conductor elements to one another.
4. The method as claimed in claim 1 , wherein the conductor elements are fixed to one another by bandaging or braiding the conductor elements.
5. The method as claimed in claim 4 , wherein bandaging or braiding the conductor elements forms a hollow interior portion within the composite superconductor, for an impregnation medium or a coolant.
6. The method as claimed in claim 1 , wherein at least some of the conductor elements are electrically isolated from one another.
7. The method as claimed in claim 1 , wherein the superconductive high-T C material is a REM 2 Cu 3 O X material, with RE being at least one element of yttrium and the rare earth metals, and M being at least one alkaline earth metal.
8. The method as claimed in claim 7 , wherein the superconductive high-T C material is a YBa 2 Cu 3 O x material.
9. A fully transposed composite superconductor produced by a process comprising:
first producing a plurality of individual shaped and coated conductor elements, each having a ribbon shape with an approximately rectangular cross section corresponding to an individual shape of the conductor element in a transposed arrangement of the composite superconductor;
wherein
each shaped and coated conductor element has at least partially a coating of a superconductive high-T C material,
each shaped and coated conductor element satisfies the relationship B<H< 20 ·B, where B is a width of the shaped and coated conductor element and H is the length of an upright bending zone of the conductor element, in a current-carrying direction in the transposed arrangement, and
upright bending of the conductor elements in the coated state is avoided; and
after producing the individual shaped and coated conductor elements, assembling the shaped and coated conductor elements to said composite superconductor in the transposed arrangement by fitting the individual shaped and coated conductor elements with one another in a process separate from producing each conductor element, wherein
the conductor elements are shaped by cutting an initial body to a desired shape, and
the initial body is coated with the superconductive high-T C material before the conductor elements are cut therefrom, to the desired shape.