Method to produce a decay resistant and weatherproof wooden product with qualities like hardwood
View Patent ↗A method to produce a decay resistant and weatherproof wooden product ( 11 ) and to its qualities like hardwood, for instance teak, in compressing and heating wood block ( 1 ) into a wanted shape. In the method a dried wood block ( 1 ) is compressed at least in one direction and the compressed wood block ( 1 kept in compressed shape, for instance between walls ( 6 ); ( 7 ), and shifted into a heating chamber, which to its cross-section is a closed chamber of predetermined shape and free from oxygen, whereby still in the said chamber the temperature of timber block ( 11 ) is quickly raised to 210–390° C. and the timber block kept tight under controlled compression in each direction and that the timber block ( 11 ), still under compression, is quickly and controllably cooled, for instance placing it in a space between cooling walls ( 8 ).
1. A method for producing a decay resistant and weatherproof wooden product having qualities like impregnated wood and hardwood, comprising the steps of:
drying a wood block;
pressing the dried wood block at least in one direction to produce a pressed wood block in a pressed shape,
shifting the pressed wood block in pressed shape, between heating walls, of a heating chamber, said heating walls forming a closed cross-section of predetermined shape and maintaining the pressed wood block in the pressed shape,
heating the pressed wood block in the pressed shape in the heating chamber free from oxygen, quickly to a temperature of 210–390° C., and maintaining the pressed wood block in the heating chamber at the temperature, and
cooling the pressed wood block in the pressed shape quickly and controllably between cooling walls of a cooling chamber.
2. A method according to claim 1 , wherein said heating and cooling steps are carried out one after another, and further including the step of shifting the pressed block in the pressed shape from between the heating walls to between the cooling walls, such that the heating and cooling walls determine outer dimensions of the pressed wood block.
3. A method according to claim 1 , further including the step of heating the wood block before said pressing step.
4. A method according to claim 1 , wherein the heating and cooling chambers are placed one after another and the heating and cooling walls form a common channel part, along which pressed wood blocks one after another are shifted through the heating and cooling chambers, a latter pressed wood block pushing a former pressed wood block one of directly or by an intermediate bearing.
5. A method according to claim 4 , further including the step of changing a cross-section profile of the pressed wood block to a desired profile by use of an intermediate bearing with a form complementary to the desired profile.
6. A method according to claim 1 :
wherein said pressing step is performed at a pressing station, and
wherein said pressing station, said heating chamber and said cooling chamber are arranged one after another in a same unit.
7. A method according to claim 1 :
wherein said pressing step is performed at a pressing station, and wherein the pressing station, the heating chamber and the cooling chamber are separate units.
8. A method according to claim 1 , further including the step if treating the dried wood block before said pressing step with a substance changing a quality of the dried wood block.
9. A method according to any claim 8 , wherein the substance is a fire retardant.
10. A method according to claim 1 , wherein a degree of moisture of the wood block prior to said pressing step is less than 18%.