Process for producing catalysts for the production of methacrylic acid
View Patent ↗In a method of producing a catalyst for the production of methacrylic acid, which has a composition of the following formula (1), when mixing 100 parts by mass of a solution or a slurry (liquid A) containing molybdenum atoms, phosphorous atoms and vanadium atoms in which the content of ammonium species is 0 to 1.5 mol relative to 12 mol of the molybdenum atoms, 5 to 300 parts by mass of a solution or a slurry (liquid B) containing 6 to 17 mol of ammonium species relative to 12 mol of the molybdenum atoms contained in the liquid A and a solution or a slurry (liquid C) containing an element Z such as cesium, the liquid B is mixed with the liquid A, the liquid C or a mixture of the liquid A and the liquid C over 0.1 to 15 minutes P a Mo b V c Cu d X e Y f Z g O h (1).
1. A method of producing a catalyst, having a composition of the following formula (1), wherein said catalyst is useful for production of methacrylic acid by subjecting methacrolein to vapor phase catalytic oxidization with molecular oxygen,
said method comprising mixing
100 parts by mass of a solution or a slurry (liquid A), containing molybdenum atoms, phosphorous atoms and vanadium atoms, in which the content of ammonium species is 0 to 1.5 mol relative to 12 mol of the molybdenum atoms,
5 to 300 parts by mass of a solution or a slurry (liquid B), containing 6 to 17 mol of ammonium species relative to 12 mol of the molybdenum atoms contained in the solution A, and
a solution or a slurry (liquid C), containing an element Z,
wherein the liquid B is mixed with the liquid A, the liquid C or a mixture of the liquid A and the liquid C over a period of 0.1 to 15 minutes:
P a Mo b V c Cu d X e Y f Z g O h (1),
wherein P, Mo, V, Cu and O represent phosphorous, molybdenum, vanadium, copper and oxygen, respectively; X represents at least one element selected from the group consisting of antimony, bismuth, arsenic, germanium, zirconium, tellurium, silver, selenium, silicon, tungsten and boron; Y represents at least one element selected from the group consisting of iron, zinc, chromium, magnesium, tantalum, cobalt, manganese, barium, gallium, cerium and lanthanum; Z represents at least one element selected from the group consisting of potassium, rubidium and cesium; a, b, c, d, e, f, g and h represent an atomic ratio of each element, and when b=12, a=0.5 to 3, c=0.01 to 3, d=0.01 to 2, e=0 to 3, f=0 to 3 and g=0.01 to 3, and h represents an atomic ratio of oxygen necessary for satisfying the valence of each of the above-mentioned components.
2. The method according to claim 1 , wherein 5 to 100 parts by mass of the liquid C is mixed with the liquid A, or a mixture of the liquid A and the liquid B over 0.1 to 30 minutes.
3. The method according to claim 1 , wherein the liquid B is a solution or a slurry which contains substantially no phosphorous, molybdenum, vanadium, copper, element X, element Y or element Z.
4. The method according to claim 1 , wherein the liquid C is a solution or a slurry which contains substantially no phosphorous, molybdenum, vanadium, copper, element X, element Y or ammonium species.
5. A catalyst for use in the production of methacrylic acid, which is produced by the method claimed in claim 1 .
6. A method of producing methacrylic acid, comprising, subjecting methacrolein to vapor phase catalytic oxidization with molecular oxygen in the presence of the catalyst for producing methacrylic acid as claimed in claim 5 .
7. The method according to claim 2 , wherein the liquid B is a solution or a slurry which contains substantially no phosphorous, molybdenum, vanadium, copper, element X, element Y or element Z.
8. The method according to claim 2 , wherein the liquid C is a solution or a slurry which contains substantially no phosphorous, molybdenum, vanadium, copper, element X, element Y or ammonium species.
9. The method according to claim 3 , wherein the liquid C is a solution or a slurry which contains substantially no phosphorous, molybdenum, vanadium, copper, element X, element Y or ammonium species.
10. A catalyst for use in the production of methacrylic acid, which is produced by the method claimed in claim 2 .
11. A catalyst for use in the production of methacrylic acid, which is produced by the method claimed in claim 3 .
12. A catalyst for use in the production of methacrylic acid, which is produced by the method claimed in claim 4 .
13. A method of producing methacrylic acid, comprising, subjecting methacrolein to vapor phase catalytic oxidization with molecular oxygen in the presence of the catalyst for producing methacrylic acid as claimed in claim 10 .
14. A method of producing methacrylic acid, comprising, subjecting methacrolein to vapor phase catalytic oxidization with molecular oxygen in the presence of the catalyst for producing methacrylic acid as claimed in claim 11 .
15. A method of producing methacrylic acid, comprising, subjecting methacrolein to vapor phase catalytic oxidization with molecular oxygen in the presence of the catalyst for producing methacrylic acid as claimed in claim 12 .