Method for controlling the temperature of a cellulosic web entering a dryer
View Patent ↗The invention relates to a method for controlling the temperature of a web, which is formed from cellulosic pulp and is to be passed to a dryer, by way of applying temperature-controlled liquid to the web. According to the invention, the thus formed web is passed into a closed space defined by two wires and side deckles, wherein temperature-controlled liquid is applied at controlled pressure and flow rate through the wire to the web.
1. A method for controlling the temperature of a web ( 5 ), which is formed from cellulosic pulp and is to be passed to a dryer, by way of applying temperature-controlled liquid to the web when passed into a closed space ( 4 ), wherein said temperature-controlled liquid ( 6 , 7 , 10 ) is applied at controlled pressure and flow rate to the web ( 5 ), wherein said closed space ( 4 ) is defined by two wires ( 1 , 2 ) and side deckles, and that said liquid is applied through the wires ( 1 , 2 ) into the web both from below the bottom wire ( 1 ) and from above the top wire ( 2 ).
2. A method according to claim 1 , wherein in the closed space ( 4 ) between the wires ( 1 , 2 ) a moderate positive pressure is maintained.
3. A method according to claim 2 , wherein the penetration of the liquid being applied into the web ( 5 ) is improved by maintaining a pressure difference between the opposite sides of the web.
4. A method according to claim 3 , wherein in order to establish said pressure difference, a suction box ( 8 , 9 ) is adapted to operate opposite to some or to each liquid feed point ( 6 , 7 , 10 ) on the other side of the web, substantially aligned with said liquid feed point ( 6 , 7 , 10 ).
5. A method according to claim 3 , wherein the temperature of the web ( 5 ) is elevated substantially close to 100° C.
6. A method according to claim 5 , wherein in order to establish said pressure difference, a suction box ( 8 , 9 ) is adapted to operate opposite to some or to each liquid feed point ( 6 , 7 , 10 ) on the other side of the web, substantially aligned with said liquid feed point ( 6 , 7 , 10 ).
7. A method according to claim 3 , wherein chemicals are added to the web ( 5 ) in conjunction with the liquid application in order to improve the qualities of the web.
8. A method according to claim 3 , wherein the solids content of the ingoing web ( 5 ) is about 0.5-4.0% and the solids of the outgoing web prior to its entry into the dryer is about 20-30%.
9. A method according to claim 2 , wherein the temperature of the web ( 5 ) is elevated substantially close to 100° C.
10. A method according to claim 9 , wherein in order to establish said pressure difference, a suction box ( 8 , 9 ) is adapted to operate opposite to some or to each liquid feed point ( 6 , 7 , 10 ) on the other side of the web, substantially aligned with said liquid feed point ( 6 , 7 , 10 ).
11. A method according to claim 2 , wherein chemicals are added to the web ( 5 ) in conjunction with the liquid application in order to improve the qualities of the web.
12. A method according to claim 2 , wherein the solids content of the ingoing web ( 5 ) is about 0.5-4.0% and the solids of the outgoing web prior to its entry into the dryer is about 20-30%.
13. A method according to claim 1 , wherein the temperature of the web ( 5 ) is elevated substantially close to 100° C.
14. A method according to claim 13 , wherein in order to establish said pressure difference, a suction box ( 8 , 9 ) is adapted to operate opposite to some or to each liquid feed point ( 6 , 7 , 10 ) on the other side of the web, substantially aligned with said liquid feed point ( 6 , 7 , 10 ).
15. A method according to claim 13 , wherein chemicals are added to the web ( 5 ) in conjunction with the liquid application in order to improve the qualities of the web.
16. A method according to claim 13 , wherein the solids content of the ingoing web ( 5 ) is about 0.5-4.0% and the solids of the outgoing web prior to its entry into the dryer is about 20-30%.
17. A method according to claim 1 , wherein chemicals are added to the web ( 5 ) in conjunction with the liquid application in order to improve the qualities of the web.
18. A method according to claim 17 , wherein the liquid is applied to the web at several successive points ( 6 , 10 ; 7 ).
19. A method according to claim 18 , wherein the liquid is applied alternatingly from above and from below the web.
20. A method according to claim 1 , wherein the solids content of the ingoing web ( 5 )is about 0.5-4.0% and the solids of the outgoing web prior to its entry into the dryer is about 20-30%.