Sliding component and method for manufacturing the same
View Patent ↗A bearing is manufactured by filling iron-based material powder and copper-based material powder in a filling portion of a mold, compacting those material powder so as to form a green compact, and then sintering the green compact. The copper-based material powder contains flat powder particles, the flat powder particles having a large aspect ratio than particles of the iron-based material powder. The coppers-based powder particles segregate on a sliding surface by vibration. The sliding surface of a bearing is covered with copper, and a ratio of iron increases from the sliding surface toward the inside. Since a rotation shaft slides on the sliding surface covered with copper, a frictional coefficient between the rotation shaft and the sliding surface is reduced, thus enabling a smooth rotation thereof. Simultaneously the usage of iron imparts predetermined strength and durability.
1. A sliding component comprising:
a sintered green compact formed from compacted iron-based material powder and copper-based material powder,
wherein said copper-based material powder contains flat powder particles of copper or copper alloy; an average value of maximum projected areas of the flat powder particles is larger than that of maximum projected areas of iron-based material powder particles; and copper is segregated on a surface of said sliding component.
2. The sliding component according to claim 1 , further comprising: a sliding portion having a surface coverage of copper greater than or equal to 60%.
3. The sliding component according to claim 2 , wherein the surface coverage of copper is greater than or equal to 90%.
4. The sliding component according to claim 1 , wherein said sliding component generates a concentration gradient in which a copper-to-iron ratio thereof decreases from the surface of the sliding component toward an inside thereof while increasing the ratio of iron to copper.
5. The sliding component according to claim 2 , wherein said one surface is a sliding surface formed in a cylindrical shape.
6. A method for manufacturing a sliding component, comprising the steps of:
filling an iron-based material powder and a copper-based material powder into a filling portion of a mold;
compacting said iron-based material powder and copper-based material powder so as to form a green compact; and
sintering said green compact,
wherein said copper-based material powder contains flat powder particles of copper or copper alloy; an average value of maximum projected areas of the flat powder particles is larger than that of maximum projected areas of iron-based material powder particles; and said flat powder particles in the filling portion are segregated on a surface of said green compact.
7. he method for manufacturing a sliding component according to claim 6 , wherein the aspect ratio of each flat powder particle is greater than or equal to 10.
8. The method for manufacturing a sliding component according to claim 7 , wherein the aspect ratio of each flat powder particle is in a range of 20 to 50.
9. The method for manufacturing a sliding component according to claim 7 , further including the step of:
segregating said flat powder particles toward the surface of said sliding component by applying vibration to said iron-based material powder and copper-based material powder filled in the filling portion of the mold.
10. The method for manufacturing a sliding component according to claim 6 , wherein a ratio of said flat powder particles to the entire material powders is in a range of 20 to 70% by weight.
11. The method for manufacturing a sliding component according to claim 7 , wherein a ratio of said flat powder particles to the entire material powders is in a range of 20 to 70% by weight.
12. The method for manufacturing a sliding component according to claim 10 , wherein the ratio of said flat powder particles to the entire material powders is in a range of 20 to 40% by weight.
13. The method for manufacturing a sliding component according to claim 6 , wherein the average value of the maximum projected areas of the flat powder particles is at least 3 times as large as that of the maximum projected areas of the iron-based material powder particles.
14. The method for manufacturing a sliding component according to claim 7 , wherein the average value of the maximum projected areas of the flat powder particles is at least 3 times as large as that of the maximum projected areas of the iron-based material powder particles.
15. The method for manufacturing a sliding component according to claim 10 , wherein the average value of the maximum projected areas of the flat powder particles is at least 3 times as large as that of the maximum projected areas of the iron-based material powder particles.