Emulsions for composite materials
View Patent ↗Emulsions are provided which are useful in imparting water-resistance to lignocellulosic composite products. In one embodiment, the emulsions comprise at least one wax, an alkyl phenol, a salt of polynaphthalenesulfonic acid, and a complexed starch. Emulsions of this embodiment may be added to hot, even boiling, water without the emulsion separating or curdling. The emulsions of the present invention are stable for extended periods of time when stored at room temperature, do not require the addition of a bactericide, and are pourable liquids at room temperature.
1. An emulsion useful in providing water-resistance to a lignocellulosic composite product, comprising:
at least one wax;
an alkyl phenol;
polynaphthalenesulfonic acid;
an alkali metal hydroxide;
water; and
a complexed starch;
wherein the alkyl phenol is a C 24 -C 34 polymerized methylene-coupled alkyl phenol.
2. The emulsion of claim 1 wherein the alkali metal hydroxide is selected from the group consisting of sodium hydroxide and potassium hydroxide.
3. The emulsion of claim 1 wherein the complexed starch is a complex of a starch and a complexing agent selected from the group consisting of a borate compound and a molybdenum compound.
4. The emulsion of claim 3 wherein the complexing agent is sodium tetraborate decahydrate.
5. The emulsion of claim 3 wherein the starch is selected from the group consisting of unmodified starch, acid-modified starch, hydroxyethylated starch, oxidized starch, and cationic starch.
6. The emulsion of claim 3 wherein the starch is acid-modified starch.
7. The emulsion of claim 5 wherein the ratio of the complexing agent to the starch on a weight per weight basis is from about 1:4 to about 1:20.
8. A lignocellulosic composite product containing the emulsion of claim 1 .
9. The lignocellulosic composite product of claim 8 wherein the lignocellulosic composite product is an oriented strand board.
10. The lignocellulosic composite product of claim 8 wherein the lignocellulosic composite product is a particle board.
11. The lignocellulosic composite product of claim 8 wherein the lignocellulosic composite product is a fiber board.
12. A method for making an emulsion useful in providing water-resistance to a lignocellulosic composite product, comprising the steps of:
(a) mixing at least one wax and an alkyl phenol to provide a first pre-mix;
(b) mixing polynaphthalenesulfonic acid, an alkali metal hydroxide, water, and a complexed starch to provide a second pre-mix;
(c) combining the first pre-mix and the second pre-mix to provide a mixture; and
(d) homogenizing the mixture;
wherein the alkyl phenol is a C 24 -C 34 polymerized methylene-coupled alkyl phenol.
13. The method of claim 12 wherein the alkali metal hydroxide is selected from the group consisting of sodium hydroxide and potassium hydroxide.
14. The method of claim 12 wherein steps (a) and (b) further comprise heating the first pre-mix and the second pre-mix to a temperature range of about 185° F. to about 195° F.
15. The method of claim 12 wherein step (d) is carried out at a pressure of at least 3500 psi.
16. The method of claim 12 wherein the complexed starch is a complex of a starch and a complexing agent selected from the group consisting of a borate compound and a molybdenum compound.
17. The method of claim 16 wherein the complexing agent is sodium tetraborate decahydrate.
18. The method of claim 16 wherein the starch is selected from the group consisting of unmodified starch, acid-modified starch, hydroxyethylated starch, oxidized starch, and cationic starch.
19. The method of claim 16 wherein the starch is acid-modified starch.
20. The method of claim 18 wherein the ratio of the complexing agent to the starch on a weight per weight basis is from about 1:4 to about 1:20.
21. An emulsion useful in providing water-resistance to a lignocellulosic composite product, comprising:
at least one wax in an amount of about 25% to about 40% by weight based on the total weight of the emulsion;
a saponifiable wax in an amount of about 2.5% to about 4.5% by weight based on the total weight of the emulsion;
an alkyl phenol in an amount of about of about 0.25% to about 10.0% by weight based on the total weight of the emulsion;
a polynaphthalenesulfonic acid in an amount of about 0.25% to about 5.0% by weight based on the total weight of the emulsion;
water in an amount of about 55% to about 65% by weight based on the total weight of the emulsion;
an alkali metal hydroxide in an amount of about 0.5% to about 1.5% by weight based on the total weight of the emulsion; and
a complexed starch, in an amount of about 1.5% to about 3.5% by weight based on the total weight of the emulsion, the complexed starch comprising a starch and a complexing agent selected from the group consisting of a borate compound and a molybdenum compound, the starch and the complexing agent having a ratio, by weight, of about 4:1 to about 20:1;
wherein the alkyl phenol is a C 24 -C 34 polymerized methylene-coupled alkyl phenol.