Resin molding and worked item therefrom
A resin molded article which is a molded article obtained by irradiating a resin molded article containing 100 to 60 parts by weight of (A) syndiotactic 1,2-polybutadiene having a crystallinity of 5% or more and 0 to 40 parts by weight of (B) another thermoplastic polymer with an electron beam, in which the 50% stress of the molded article after the electron beam irradiation (50% M:M2) is from 1.01 to 2.5 times the 50% stress before the electron beam irradiation (50% M:M1), and the molded article has steam sterilization resistance. The molded article is excellent in flexibility and hardness, excellent in steam sterilization resistance, and useful for medical applications such as an infusion tube, an infusion solution container, a catheter and the like.
1. An irradiated resin molded article for medical applications which is crosslinked by irradiating, with an electron beam, said resin molded article comprising
100 parts by weight of (A) syndiotactic 1,2-polybutadiene having a crystallinity of 5% or more,
0 parts by weight of (B) at least one thermoplastic polymer selected from the group of polypropylene, a styrene-butadiene-styrene block copolymer, a styrene-isoprene-styrene block copolymer, a hydrogenerated styrene-butadiene-styrene block copolymer, a hydrogenated styrene-isoprene-styrene block co-polymer, a polybutadiene other than the syndiotactic 1,2-polybutadiene, an acrylonitrile-butadiene-styrene resin, a polyisoprene, a polyethylene, an ethylene-vinyl acetate copolymer, an ethylene-acrylate ester copolymer and an ethylene-methacrylate copolymer,
with the proviso that (A)+(B)=100 parts by weight,
in which the irradiation dose of the electron beam is from 5 to 200 in Mrad,
in which the energy of the electron beam is from 20 to 5,000 kV,
wherein the tensile stress at the 50% point of the tensile strength curve of the irradiated resin molded article, as measured in MPa, is from 1.01 to 2.5 times the tensile stress at the 50% point of the tensile strength curve, as measured in MPa, of the resin molded article, and
wherein the irradiated resin molded article has steam sterilization resistance.
2. The irradiated resin molded article according to claim 1 , which has transparency that the haze value of a 2-mm sheet is 50 or less.
3. The irradiated resin molded article according to claim 2 , which has a toluene insoluble matter after the electron beam irradiation of 50 to 99% by weight.
4. The irradiated resin molded article according to claim 3 , wherein the shape of the molded article is at least one selected from the group of a tube, a sheet, a film, a bag and a connector.
5. The irradiated resin molded article according to claim 4 , which is for medical applications.
6. The irradiated resin molded article according to claim 5 , which has a halogen atom content of 50 ppm or less.
7. The irradiated resin molded article according to claim 1 , which has a toluene insoluble matter after the electron beam irradiation of 50 to 99% by weight.
8. The irradiated resin molded article according to claim 1 , wherein as for electron beam dose, the product of electron beam acceleration voltage in kV and irradiation dose in Mrad is from 2 to 1,000,000 kVMrad.
9. The irradiated resin molded article according to claim 8 , which has transparency that the haze value of a 2-mm sheet is 50 or less.
10. The irradiated resin molded article according to claim 1 , which has a halogen atom content of 50 ppm or less.
11. The irradiated resin molded article according to claim 1 , wherein the shape of the molded article is at least one selected from the group of a tube, a sheet, a film, a bag and a connector.
12. The irradiated resin molded article according to claim 1 , which has a halogen atom content of 50 ppm or less.
13. A processed product obtained by processing an irradiated resin molded article obtained by irradiating a resin molded article, with an electron beam, the resin molded article comprising
100 parts by weight of (A) syndiotactic 1,2-polybutadiene having a crystallinity of 5% or more, and
0 parts by weight of (B) at least one thermoplastic polymer selected from the group of polypropylene, a styrene-butadiene-styrene block copolymer, a styrene-isoprene-styrene block copolymer, a hydrogenerated styrene-butadiene-styrene block copolymer, a hydrogenated styrene-isoprene-styrene block copolymer, a polybutadiene other than the syndiotactic 1,2-polybutadiene, an acrylonitrile-butadiene-styrene resin, a polyisoprene, a polyethylene, an ethylene-vinyl acetate copolymer, an ethylene-acrylate ester copolymer and an ethylene-methacrylate copolymer,
with the proviso that (A)+(B)=100 parts by weight
in which the irradiation dose of the electron beam is from 5 to 200 in Mrad,
wherein the tensile stress at the 50% point of the tensile strength curve of the irradiated molded article, as measured in MPa, is from 1.01 to 2.5 times the tensile stress at the 50% point of the tensile strength curve, as measured in MPa, of the resin molded article, and
wherein the irradiated molded article has steam sterilization resistance.