Enteric composition for the manufacture of soft capsule wall
View Patent ↗A gel mass is provided that is useful in manufacturing enteric soft or hard capsules, or enteric tablets without coating.
1. An enteric soft capsule shell formed from a gel mass composition comprising
(a) a film-forming, water-soluble polymer,
(b) an acid-insoluble polymer; and
(c) an alkaline aqueous solvent;
wherein the ratio of acid-insoluble polymer to film-forming, water soluble polymer is from 30:70 to 45:55 by weight;
the final pH of the gel mass is less than or equal to about 9 pH units;
and the moisture content of the enteric soft capsule shell formed from the gel mass composition is from about 2% to about 10%.
2. The enteric soft capsule shell of claim 1 , wherein the film-forming, water-soluble polymer is proteinaceous.
3. The enteric soft capsule shell of claim 2 , wherein the proteinaceous film-forming, water-soluble polymer is gelatin.
4. The enteric soft capsule shell of claim 3 , wherein the gelatin is extracted from animal bones or skins, and has about 100 to about 250 blooms.
5. The enteric soft capsule shell of claim 1 , wherein the film-forming, water-soluble polymer is a carbohydrate.
6. The enteric soft capsule shell of claim 5 , wherein the carbohydrate is selected from the group consisting of hydroxypropyl methylcellulose and methyl cellulose.
7. The enteric soft capsule shell of claim 1 , wherein the acid-insoluble polymer is selected from the group consisting of acrylic and methacrylic acid copolymers, cellulose acetate esters, hydroxypropyl methyl cellulose phthalate, and salts thereof.
8. The enteric soft capsule shell of claim 1 , further comprising at least one plasticizer selected from the group consisting of sorbitol, glycerol, polyethylene glycol, poly-alcohols with 3 to 6 carbon atoms, citric acid, citric acid esters, triethyl citrate, and combinations thereof.
9. The enteric soft capsule shell of claim 1 , wherein the alkaline aqueous solvent comprises an alkali selected from the group consisting of ammonia, sodium hydroxide, potassium hydroxide, ethylenediamine, hydroxylamine, and tri-ethanolamine.
10. The enteric soft capsule shell of claim 1 , wherein the alkaline aqueous solvent comprises a volatile alkali.
11. The enteric soft capsule shell of claim 10 , wherein the volatile alkali is selected from the group consisting of ammonia and ethylenediamine.
12. The enteric soft capsule shell of claim 1 , wherein the alkaline aqueous solvent is a hydroalcoholic solution.
13. The enteric soft capsule shell of claim 1 , where the final pH of the gel mass is less than or equal to about 8.5.
14. The enteric soft capsule shell of claim 1 , wherein the enteric soft capsule shell has a moisture content of from about 2% to about 10%.
15. The enteric soft capsule shell of claim 14 , wherein the moisture content is from about 4% to about 8%.
16. The enteric soft capsule shell of claim 14 , wherein the moisture content is about 8%.
17. The enteric soft capsule shell of claim 1 , wherein the gel mass composition comprises a plasticizer, and the ratio of plasticizer to film-forming, water-soluble polymer is from about 1:9 to about 1:1 by weight.
18. The enteric soft capsule shell of claim 17 , wherein the ratio of plasticizer to film-forming, water-soluble polymer is about 1:3 by weight.