Permselective membrane and process for manufacturing thereof
View Patent ↗The present invention relates to a membrane being suitable for, for example, hemodialysis. Said membrane comprises at least one hydrophobic polymer and at least one hydrophilic polymer. According to the present invention the outer surface of the hollow fiber has pores in the range of 0.5-3 μm and the numbers of said pores in the outer surface are in the range of 10,000 to 150,000 pores per mm 2 , preferably in the range of 18,000 to 100,000 pores per mm 2 , and most preferably in the range of 20,000 to 100,000 pores per mm 2 . The present invention further relates to a process for the preparation of said membrane and use of said membrane in hemodialysis, hemodiafiltration and hemofiltration, and in dialysis and filtration in general, for example in water purification or dehydration.
1. A permselective asymmetric hollow fiber membrane suitable for hemodialysis comprising at least one hydrophobic polymer and at least one hydrophilic polymer, said hollow fiber membrane consisting of a first inner separation layer in the form of a dense rather thin layer including pores having a pore size in the range of 5-20 nm, a second layer in the form of a sponge structure, a third layer in the form of a finger structure, and a fourth outer layer in the form of a sponge layer having an outer surface having pores with sizes in the range of 0.5-3 μm, the number of said pores on the outer surface of the sponge layer being in the range of 10,000 to 150,000 pores per mm 2 .
2. A membrane according to claim 1 , wherein said membrane has a diffusive permeability of urea of 15-17×10 −4 cm/sec measured at 37° C.
3. A membrane according to claim 1 , wherein said first separation layer has a thickness less than 1 μm, said second layer has a thickness of about 1 to 15 μm, said third layer has a thickness of about 20 to 60 μm, and said fourth outer layer has a thickness of about 1 to 10 μm.
4. A membrane according to claim 1 , wherein said membrane is 65-95% by weight of said at least one hydrophobic polymer and 5-35% by weight of said at least one hydrophilic polymer.
5. A membrane according to claim 1 , wherein said at least one hydrophobic polymer is chosen from a group of polymers consisting of polyamide (PA), polyaramide (PAA), polyarylethersulphone (PAES), polyethersulphone (PES), polysulphone (PSU), polyarylsulphone (PASU), polycarbonate (PC), polyether, polyurethane (PUR), polyetherimide, and copolymers of said polymers.
6. A membrane according to claim 1 , wherein the at least one hydrophilic polymer is chosen from the group consisting of polyvinylpyrrolidone (PVP), polyethylene glycol (PEG), polyglycolmonoester, water soluble cellulosic derivates, polysorbate, and polyethylene-polypropylene oxide copolymers.
7. A membrane according to claim 1 configured for hemodiafiltration and hemofiltration.
8. A membrane according to claim 1 configured for dialysis and filtration.
9. A membrane according to claim 1 , wherein the density of pores on the outer surface are in the range of 18,000 to 100,000 pores per mm 2 .
10. A membrane according to claim 1 , wherein the density of pores on the outer surface are in the range of 20,000 to 100,000 pores per mm 2 .
11. A membrane according to claim 2 , wherein said first separation layer has a thickness less than 1 μm, said second layer has a thickness of about 1 to 15 μm, said third layer has a thickness of about 20 to 60 μm, and said fourth outer layer has a thickness of about 1 to 10 μm.
12. A membrane according to claim 5 , wherein the at least one hydrophilic polymer is chosen from the group consisting of polyvinylpyrrolidone (PVP), polyethylene glycol (PEG), polyglycolmonoester, water soluble cellulosic derivates, polysorbate, and polyethylene-polypropylene oxide copolymers.