Composition prepared from silica sol and mineral acid
View Patent ↗The present invention relates to a method of preparing a composition comprising mixing a silica sol having an S-value from about 5 to about 50% and a mineral acid. The invention also relates to a composition obtainable by the method and a composition comprising a network of silica particles and mineral acid, wherein the silica particles have a particle size of from about 2 to about 7 nm. The invention also relates to the use of the composition as a gelled electrolyte.
1. Method of preparing a composition comprising mixing a silica sol having an S-value from about 15 to about 45% and a mineral acid, wherein the weight ratio of silica to mineral acid is from about 1:100 to about 25:100.
2. Method according to claim 1 , wherein the S-value is from about 15 to about 40%.
3. Method according to claim 1 , wherein the S-value is from about 15 to about 35%.
4. Method according to claim 1 , wherein the silica sol has a specific surface area from about 400 to about 1200 m 2 /g.
5. Method according to claim 1 , wherein the silica sol has a specific surface area from about 500 to about 1000 m 2 /g.
6. Method according to claim 1 , wherein the silica sol has a specific surface area from about 600 to about 900 m 2 /g.
7. Method according to claim 1 , wherein the mineral acid is sulphuric acid.
8. Method according to claim 1 , wherein the mineral acid is hydrochloric acid, nitric acid, phosphoric acid, and mixtures thereof.
9. Method according to claim 1 , wherein orthophosphoric acid and/or sodium sulphate is further added.
10. Method according to claim 1 , wherein the content of chloride in the silica sol is lower than about 50 ppm by weight.
11. Method according to claim 1 , wherein the mineral acid has a pH ranging from about −2 to about 2.
12. Method according to claim 11 , wherein the mineral acid has a pH ranging from about −1.5 to about 1.