Particle size and morphology control in rubber modified monovinylidene aromatic polymers
The present invention is a mass/solution polymerization process to produce a rubber modified polymer, having rubber particle size, distribution and morphology control, at an increased rate, utilizing functionalized diene rubbers, wherein the functionality enables controlled radical polymerization.
1 . A mass/solution polymerization process utilizing a functionalized rubber to produce a rubber modified polymer from a vinyl aromatic monomer comprising polymerizing the vinyl aromatic monomer in the presence of a rubber, wherein the rubber comprises a functionalized diene rubber having:
a) a solution viscosity of from 5 to less than 50 centipoise (cps), and
b) at least one functional group per rubber molecule which enables controlled radical polymerization;
such that grafted rubber particles are formed and dispersed within a matrix comprising polymerized vinyl aromatic monomer and have a broad monomodal size distribution.
2 . The process of claim 1 wherein the vinyl aromatic monomer is styrene.
3 . The process of claim 1 wherein the vinyl aromatic monomer is copolymerized with acrylonitrile.
4 . The process of claim 1 wherein the functionalized diene rubber is a styrene/butadiene block copolymer rubber.
5 . The process of claim 1 wherein the functionalized diene rubber has a solution viscosity of 5 weight percent in styrene at 20° C. of less than 45 cps.
6 . The process of claim 1 wherein the functionalized diene rubber contains a functional group capable of forming a stable free radical.
7 . The process of claim 6 wherein the functionalized diene rubber contains a nitroxide functional group.
8 . The process of claim 6 wherein the functionalized diene rubber contains a functional group selected from 2,2,6,6,-tetramethyl-1-piperidinyloxy (TEMPO); 2,2,6,6-tetramethyl-1-[1-[4-(oxiranylmethoxy)phenyl]ethoxy]-piperidine; or 3,3,8,8,10,10-hexamethyl-9-[1-[4-(oxiranylmethoxy)phenyl]ethoxy]-1,5-dioxa-9-azaspiro[5.5]undecane.
9 . The process of claim 1 wherein the functionalized diene rubber contains a functional group capable of atom transfer radical polymerization.
10 . The process of claim 1 wherein the functionalized diene rubber contains a functional group capable of reversible addition-fragmentation chain transfer polymerization.
11 . The process of claim 1 wherein the polymerization is conducted in the presence of a chain transfer agent.
12 . The process of claim 1 wherein the polymerization is conducted in the presence of an initiator.
13 . The process of claim 1 wherein the polymerization is conduction in the presence of an initiator and a chain transfer agent.
14 . (canceled)
15 . (canceled)
16 . (canceled)
17 . The process of claim 1 wherein a portion of a partially polymerized feed is recirculated to an earlier polymerization stage.
18 . The rubber modified polymer produced by the process of claim 1 .
19 . An article or composition comprising the rubber modified polymer of claim 18.