Fluoropolymer-containing sol-gel coating
View Patent ↗A sol-gel coating composition comprising fluoropolymer particles is disclosed. The fluoropolymer particles are distributed homogeneously in the coating, leading to scratch-resistant anti-stick and low-friction coatings that are suitable, for example, for electrical and non-electrical domestic appliances.
1. A coated article comprising a substrate coated with a sol-gel coating, the sol-gel coating, based on a sol-gel precursor comprising fluoropolymer particles, said coating having hydrophobic properties such that the contact angle of water at the surface thereof is at least 88°, wherein the coated article comprises a domestic appliance, and wherein the fluoropolymer particles of the sol-gel coating are stabilized with a polysiloxane polyoxyalkylene copolymer.
2. The coated article according to claim 1 , wherein a contact angle of water at the surface of the sol-gel coating is at least 90°.
3. The coated article according to claim 1 , wherein a contact angle of water at the surface of the sol-gel coating is at least 94°.
4. The coated article according to claim 1 , wherein the sol-gel coating comprises filler particles.
5. The coated article according to claim 4 , the filler particles comprise silica particles originating from an aqueous silica sol.
6. The coated article according to claim 1 , wherein the volume fraction of fluoropolymer particles of the sol-gel coating is below 50%.
7. The coated article according to claim 6 , characterized in that the volume fraction of fluoropolymer particles is in the range of 15-30%.
8. The coated article according to claim 1 , wherein the fluorocarbon particles of the sol-gel coating comprise polytetrafluoroethylene particles.
9. The coated article according to claim 1 , wherein the sol-gel coating is based on a hybrid sol-gel precursor, comprising an organosilane compound.
10. The coated article according to claim 1 , wherein the sol-gel precursors comprise, methyltri(m)ethoxysilane, phenyltri(m)ethoxysilane, diphenyldi(m)ethoxysilane, glycidoxypropyl-tri(m)ethoxysilane, or combinations thereof.
11. The coated article according to claim 1 , wherein the sol-gel coating is temperature-resistant up to 400° C.
12. The coated article according to claim 1 , wherein the substrate is a metal substrate.
13. The coated article according to claim 12 wherein the metal substrate is an aluminum or an aluminum alloy.
14. A coated article according to claim 1 , characterized in that it belongs to a group comprising steam irons, vacuum cleaners, fans and domestic air treatment devices, kettles and coffee makers, mixers and food processors, toasters and sandwich makers, ice cream makers, deep fat fryers, grills and electric gourmet sets and woks, rice cookers, pots and pans, and cooking utensils.
15. Method of preparing a sol-gel coating, comprising the steps of: acidifying a silica sol to a pH value of about 3; adding part of a total amount of sol-gel precursor sufficient to stabilize the silica particles; hydrolyzing and stabilizing of the mixture; adding the rest of the total amount of sol-gel precursor; hydrolyzing the mixture; and adding fluoropolymer dispersion.
16. Method according to claim 15 , characterized in that the fluoropolymer particles are stabilized with a polysiloxane polyoxyalkylene copolymer.
17. A coated article comprising a substrate coated with a sol-gel coating, the sol-gel coating composition comprising a sol-gel precursor and a stabilized aqueous dispersion of fluoropolymer particles, wherein the stabilizer is a polysiloxane polyoxyalkylene copolymer, characterized in that the coated article comprises a domestic appliance.
18. A coated article comprising a substrate coated with a sol-gel coating, the a sol-gel coating based on a coating composition comprising a sol-gel precursor and a stabilized aqueous dispersion of fluoropolymer particles, wherein the stabilizer is a polysiloxane polyoxyalkylene copolymer, characterized in that the coated article comprises a domestic appliance.