Controlling or modeling a chemical vapor infiltration process for densifying porous substrates with carbon
View Patent ↗A load comprising one or more porous substrates ( 10 ) for densification is heated in an oven into which a reaction gas containing at least one carbon-precursor hydrocarbon is admitted, the effluent gas being extracted from the oven via an extraction pipe ( 26 ) connected to an outlet from the oven. The content in the effluent gas of at least one compound selected from allene, propine, and benzene is measured, and as a function of the measured content, the process is controlled by adjusting at least one parameter selected from the rate at which the reaction gas is admitted into the oven, the rate at least one component of the reaction gas is admitted into the oven, the transit time of the gas through the oven, the temperature to which the substrate(s) is/are heated, and the pressure that exists inside the oven. The at least one parameter is adjusted in such a manner as to maintain the measured content at a value which is substantially constant. A densification process can thus be controlled in real time or modelled.
1. A method of controlling or modeling the process of densifying at least one porous substrate with pyrolytic carbon by chemical vapor infiltration, the process comprising: placing a load comprising one or more porous substrates to be densified in an oven; heating the substrate(s); admitting a reaction gas into the oven, the reaction gas containing at least one carbon-precursor hydrocarbon selected in the group of propane, butane, propylene and ethane; adjusting the pressure in the oven so as to enable the gas to diffuse within the pores of the heated substrate(s) so as to form a deposit of pyrolytic carbon therein; and extracting effluent gas from the oven via an extraction pipe connected to an outlet from the oven;
the method being characterized by measuring the content in the effluent gas of at least one compound selected from allene and propine; and controlling the process by adjusting at least the flow rate of the carbon-precursor hydrocarbon admitted into the oven to maintain the measured content at a substantially constant value.
2. A method according to claim 1 , wherein the content is measured in a duct in parallel with the extraction pipe.
3. A method according to claim 1 , wherein the content is measured by gas chromatography.
4. A method according to claim 1 , wherein the carbon-precursor hydrocarbon is diluted in methane or in an inert gas.
5. A method according to claim 1 , wherein the flow rate is adjusted within a predetermined range of values.
6. A method according to claim 5 , wherein the end of the densification process is detected by it becoming impossible to control the variation in the measured content by adjusting the flow rate.
7. A method according to claim 1 , wherein the variation in the flow rate is stored so as to constitute a model that is reproducible during a subsequent process of densifying a load of the same type.
8. A method according to claim 7 wherein the end of the densification process is detected by it becoming impossible to control the variation in the measured content by adjusting the flow rate and that the duration of the densification process is also stored.
9. A method of controlling or modeling the process of densifying at least one porous substrate with pyrolytic carbon by chemical vapor infiltration, the process comprising: placing a load comprising one or more porous substrates to be densified in an oven; heating the substrate(s); admitting a reaction gas into the oven, the reaction gas containing at least one carbon-precursor hydrocarbon; adjusting the pressure in the oven so as to enable the gas to diffuse within the pores of the heated substrate(s) so as to form a deposit of pyrolytic carbon therein; and extracting effluent gas from the oven via an extraction pipe connected to an outlet from the oven;
the method being characterized by measuring the content in the effluent gas of at least one compound selected from allene, propine, and benzene; and, as a function of the measured content, by controlling the process by adjusting at least one parameter selected from: the flow rate of the reaction gas admitted into the oven, the flow rate of at least one component of the gas admitted into the oven, the transit time of the gas through the oven, the temperature to which the substrate(s) is/are heated, and the pressure that exists inside the oven,
wherein the selected parameter is adjusted within a predetermined range of values, and
wherein the end of the densification process is detected by it becoming impossible to control the variation in the measured content by adjusting the selected parameter.