Process for producing rare earth oxide superconductor
View Patent ↗RE superconductive layer of high critical current density (Jc) is superimposed on an interlayer formed so as to, while ensuring cracking prevention, excel in crystallinity, such as in-plane orientation degree and direction, and surface smoothness. On an oriented Ni substrate, there are sequentially superimposed an interlayer of cerium oxide loaded with 20 to 60 mol %, in terms of metal content, of one or at least two rare earth elements according to MOD technique and an RE superconductive layer of high Jc according to MOD technique. The above interlayer is formed by mixing a Gd, Y and/or Yb organometallic compound solution with a Ce organometallic compound solution, applying the mixed solution onto an oriented Ni substrate so as to form a coating film and subjecting the coating film to calcination heat treatment and thereafter firing in an Ar—H 2 atmosphere at 950 to 1150° C. under a pressure of 50 to 500 Pa. YBCO superconductive layer is formed on this interlayer according to TFA-MOD technique.
1. A process for producing a rare earth oxide superconductor, comprising:
mixing cerium with 5 to 90 mol %, in terms of the metal content, of at least one rare earth element Re selected from the group consisting of Y, Nd, Sm, Gd, Eu, Yb, Ho, Tm, Dy, La and Er;
applying the mixture onto a surface of a metal substrate by liquid phase, metal organic deposition;
calcining the applied mixture at a temperature of 900° C. or higher and lower than 1200° C. under a reduced pressure of 0.1 Pa or higher and lower than atmospheric pressure to form an intermediate layer comprising a cerium oxide; and then
forming a rare earth oxide superconducting layer on the intermediate layer.
2. The process for producing a rare earth oxide superconductor according to claim 1 , wherein the content of the rare earth element Re in the mixture is 20 to 60 mol %, in terms of the metal content.
3. The process for producing a rare earth oxide superconductor according to claim 1 , wherein the intermediate layer is formed by calcination under a pressure ranging from 50 to 500 Pa.
4. The process for producing a rare earth oxide superconductor according to claim 1 , wherein the intermediate layer is formed by calcination at a temperature ranging from 950 to 1150° C.
5. The process for producing a rare earth oxide superconductor according to claim 1 , wherein metal substrate is a biaxially textured metal substrate.
6. The process for producing a rare earth oxide superconductor according to claim 1 , wherein the rare earth oxide superconducting layer is directly formed on the intermediate layer.
7. The process for producing a rare earth oxide superconductor according to claim 1 wherein the calcining is at a temperature of 950-1150° C.
8. A process for producing a rare earth oxide superconductor, comprising:
mixing cerium with 20 to 60 mol %, in terms of metal content, of at least one rare earth element Re selected from the group consisting of Y, Nd, Sm, Gd, Eu, Yb, Ho, Tm, Dy, La and Er;
applying the mixture onto a surface of a biaxially textured metal substrate by metal organic deposition;
calcining the applied mixture and in a reducing gas atmosphere containing 0.1 to 10% H 2 , Ar and N 2 , at a temperature from 950 to 1150° C. and under a pressure from 50 to 500 Pa, to form an intermediate layer comprising a cerium oxide; and then
forming a rare earth oxide superconducting layer on the intermediate layer.