Chlorinated vinyl chloride resin composition
View Patent ↗A chlorinated vinyl chloride-based resin composition in which from 2 to 9 parts by weight of an MBS resin and from 0.5 to 3 parts by weight of chlorinated polyethylene are blended to 100 parts by weight of a chlorinated vinyl chloride-based resin with a chlorine content of from 62 to 70% by weight obtained by post-chlorinating a vinyl chloride-based resin, which can provide an injection molding product such as a joint of excellent heat resistance, impact strength, moldability and surface property.
1. A chlorinated vinyl chloride-based resin composition for use in injection molding in which
from 2 to 9 parts by weight of an MBS resin and from 0.5 to 3 parts by weight of chlorinated polyethylene are blended to 100 parts by weight of a chlorinated vinyl chloride-based resin with a chlorine content of from 62 to 70% by weight obtained by post-chlorinating a vinyl chloride-based resin;
wherein an acrylic resin for improving the processability of vinyl chloride is further added to the blend, said acrylic resin comprises polymethyl methacrylate as a main ingredient and has a specific viscosity at 30° C. of not exceeding 1.5 when 0.4 g thereof is dissolved in 100 ml of benzene.
2. A chlorinated vinyl chloride-based resin composition for use in injection molding in which
from 2 to 9 parts by weight of an MBS resin and from 0.5 to 3 parts by weight of chlorinated polyethylene are blended to 100 parts by weight of a chlorinated vinyl chloride-based resin with a chlorine content of from 62 to 70% by weight obtained by post-chlorinating a vinyl chloride-based resin;
wherein an acrylic resin for improving the processability of vinyl chloride is further blended by from 0.5 to 3 parts by weight to the blend; and
wherein the acrylic resin for improving the processability of vinyl chloride comprises polymethyl methacrylate as a main ingredient and has a specific viscosity at 30° C. of not exceeding 1.5 when 0.4 g thereof is dissolved in 100 ml of benzene.
3. A chlorinated vinyl chloride-based resin composition for use in injection molding in which
from 2 to 9 parts by weight of an MBS resin and from 0.5 to 3 parts by weight of chlorinated polyethylene are blended to 100 parts by weight of a chlorinated vinyl chloride-based resin with a chlorine content of from 67 to 69% by weight obtained by post-chlorinating a vinyl chloride-based resin of an average polymerization degree of 650 or less;
wherein an acrylic resin for improving the processability of vinyl chloride is further added to the blend, said acrylic resin comprises polymethyl methacrylate as a main ingredient and has a specific viscosity at 30° C. of not exceeding 1.5 when 0.4 g thereof is dissolved in 100 ml of benzene.
4. A chlorinated vinyl chloride-based resin composition according to claim 1 , wherein the butadiene content of the MBS resin is larger than 60% by weight.
5. A chlorinated vinyl chloride-based resin composition according to claim 1 , wherein the chlorine content of the chlorinated polyethylene is from 20 to 45% by weight.
6. A chlorinated vinyl chloride-based resin composition according to claim 1 , wherein the Vicat softening point at a load of 5 kg is 105° C. or higher.
7. A heat resistant joint comprising a chlorinated vinyl chloride-based resin composition according to claim 1 .
8. A chlorinated vinyl chloride-based resin composition according to claim 2 , which uses a chlorinated vinyl chloride-based resin with a chlorine content of from 67 to 69% by weight obtained by post-chlorinating a vinyl chloride-based resin of an average polymerization degree of 650 or less.
9. A chlorinated vinyl chloride-based resin composition according to claim 2 , wherein the butadiene content of the MBS resin is larger than 60% by weight.
10. A chlorinated vinyl chloride-based resin composition according to claim 2 , wherein the chlorine content of the chlorinated polyethylene is from 20 to 45% by weight.
11. A chlorinated vinyl chloride-based resin composition according to claim 2 , wherein the Vicat softening point at a load of 5 kg is 105° C. or higher.
12. A chlorinated vinyl chloride-based resin composition according to claim 2 , wherein the butadiene content to 100 parts of the chlorinated vinyl chloride-based resin is 1 part by weight or more and 6 parts by weight or less.
13. A heat resistant joint comprising a chlorinated vinyl chloride-based resin composition according to claim 2 .
14. A chlorinated vinyl chloride-based resin composition according to claim 3 , wherein the butadiene content of the MBS resin is larger than 60% by weight.
15. A chlorinated vinyl chloride-based resin composition according to claim 3 , wherein the chlorine content of the chlorinated polyethylene is from 20 to 45% by weight.
16. A chlorinated vinyl chloride-based resin composition according to claim 3 , wherein the Vicat softening point at a load of 5 kg is 105° C. or higher.
17. A chlorinated vinyl chloride-based resin composition according to claim 3 , wherein the butadiene content to 100 parts of the chlorinated vinyl chloride-based resin is 1 part by weight or more and 6 parts by weight or less.
18. A heat resistant joint comprising a chlorinated vinyl chloride-based resin composition according to claim 3 .