Cellulose-based microporous membrane
View Patent ↗There is disclosed a cellulosic microporous filtration membrane with upper and lower porous protective layers with a porous sponge-type intermediate layer between the two protective layers, wherein the sponge-type structure consists of two isotropic regions having different pore sizes.
1. An asymmetric cellulosic microporous membrane having three distinct regions comprising (i) a porous upper layer, (ii) a porous lower layer, and (iii) a porous intermediate portion between said upper and lower layers, wherein said intermediate portion has a first isotropic region adjacent the upper layer and a second isotropic region adjacent the lower layer, and wherein
the pores of the said first isotropic region are smaller than the pores in said upper layer but larger than the pores in said second isotropic region; and
the pores of said second isotropic region are smaller than the pores in said lower layer
and wherein said membrane is formed from a casting solution comprising a cellulose acetate, a solvent selected from methyl formate and methyl acetate and a non-solvent and, following casting, is dried with an inert gas.
2. The membrane of claim 1 wherein the pore density in said upper and lower layers ranges from 1×10 4 to 1×10 6 pores/mm 2 .
3. The membrane of claim 2 wherein the pore density in said upper layer ranges from 1×10 4 to 5×10 5 pores/mm 2 and the pore density in the lower layer ranges from 3×10 5 to 1×10 6 pores/mm 2 .
4. The membrane of claim 2 wherein the median diameter of the pores in said upper layer ranges from 0.4 to 15 μm and the median diameter of the pores in said lower layer ranges from 0.1 to 3.0 μm.
5. The membrane of claim 4 wherein the median pore diameter of said pores in said first and second isotropic regions differ by a factor of 1.4 to 16.
6. The membrane of claim 5 wherein one of said first and second isotropic regions constitutes 20% to 80% of the thickness of said intermediate layer.
7. The membrane of any of claims 1 - 3 , 4 or 5 - 6 wherein said cellulosic microporous membrane comprises a cellulose acetate selected from the group consisting of cellulose triacetate, cellulose diacetate, and mixtures thereof.
8. The membrane of claim 7 wherein said cellulosic microporous membrane comprises a mixture of (i) cellulose triacetate having an acetylation level of from 58% to 62.5%, and (ii) cellulose diacetate having an acetylation level in a range from 51% to 57%, and wherein the weight ratio of (i):(ii) is from 1.5:1 to 0.8:1.
9. The membrane of claim 8 further comprising a reinforcement material integrated into said membrane.