Method for processing surfaces of aluminium alloy sheets and strips
A method for processing the surface of a strip, sheet or a shaped part made of an aluminum alloy which involves the preparation of a surface with the aid of an atmospheric pressure plasma and by a chemical conversion treatment using at least the elements Si, Ti, Zr, Ce, Co, Mn, Mo and V, for producing a conversion coating on the strip, sheet or part. The process is more rapid and less costly than previous conversion treatments and is applied, in particular, for strips and sheets which are used for a car body and assembled by welding or gluing.
1 . Process for the surface treatment of a strip, a sheet or a stamped part of a sheet or a strip made of an aluminium alloy consisting of a surface preparation using an atmospheric plasma and a chemical conversion treatment using at least one of the elements Si, Ti, Zr, Ce, Co, Mn, Mo or V to form the conversion layer on the strip, the sheet or the part.
2 . Process according to claim 1 , characterised in that the aluminium alloy is an alloy in the 5000 series or 6000 series.
3 . Process according to claim 1 , characterised in that the conversion treatment is done using at least one salt of one of at least the said elements.
4 . Process according to claim 3 , characterised in that the conversion treatment is done by immersion in the bath.
5 . Process according to claim 3 , characterised in that the conversion treatment is done by atomisation of the bath on the strip, the sheet or the part.
6 . Process according to claim 3 , characterised in that the conversion treatment is done by coating the strip, the sheet or the part with the bath.
7 . Process according to claim 3 , characterised in that the treatment bath has a pH of between 3 and 11.
8 . Process according to claim 1 , characterised in that the conversion treatment is done using an atmospheric plasma using a plasmagenic gas including a compound of at least one of the elements Si, Al, Ti, Zr, Ce, Co, Mn, Mo or V.
9 . Process according to claim 1 , characterised in that the treatment rate is from 5 m/min to 600 m/min.
10 . Process according to claim 1 , characterised in that the conversion layer has a thickness of between 5 and 300 nm.
11 - 12 . (canceled)