Polymerization process involving the dosing initiators
View Patent ↗The invention relates to a polymerization process wherein at least one peroxide, with a half life in between 1 hour and 0.001 hour at the polymerization temperature at the moment of dosing, is dosed to the reaction mixture at the polymerization temperature and wherein at least during part of the period in which the peroxide is dosed i) the cooling means of the reactor are kept at essentially maximum cooling capacity and ii) the amount of initiator that is dosed is actively controlled such that the desired polymerization temperature is achieved and maintained within 0.3° C. of said polymerization temperature.
1. A polymerization process comprising:
achieving a desired polymerization temperature of a reaction mixture in a reactor;
dosing at least one peroxide over a period of time to the reaction mixture at the desired polymerization temperature, the peroxide having half life in between 1 hour and 0.001 hour at the desired polymerization temperature, wherein at least during part of the period in which the peroxide is dosed:
cooling means of the reactor are kept at essentially maximum cooling capacity; and
the amount of initiator that is dosed is actively controlled by a temperature controller such that the temperature of the reaction mixture is achieved and maintained within 0.3° C. of the desired polymerization temperature.
2. The polymerization process of claim 1 wherein the temperature of the reaction mixture is maintained within 0.2° C. of the desired polymerization temperature.
3. The polymerization process of claim 1 wherein the temperature controller controls the temperature of the reaction mixture by monitoring the temperature of the reaction mixture and/or the pressure of any gas phase in the reactor during the polymerization reaction, while at the same time adjusting the dosing rate of the initiator to the reaction mixture.
4. The polymerization process of claim 1 wherein the polymer obtained has a K-value within 0.3 units of the desired K-value.
5. The polymerization process of claim 1 wherein the temperature is controlled by a temperature controller selected from the group consisting of a PID controller, a PI controller, a PD controller, and a fuzzy logic controller.
6. A polymerization process according to claim 5 wherein the controller is a PID controller using a proportional band, and the proportional band of the PID controller is in the range of from 0.6% to 2.5%.
7. A polymerization process according to claim 6 wherein temperature sensing means are linked to the proportional and integral input signals of the PID controller and wherein reactor pressure sensing means are linked to a derivative function of the PID controller during at least part of the period in which the peroxide is dosed.
8. A polymerization process according to claim 1 wherein vinyl chloride is polymerized, optionally together with other monomers.
9. A polymerization process according to claim 1 wherein the polymerization process is a suspension polymerization process.
10. The polymerization process of claim 1 , wherein the temperature of the reaction mixture is maintained within 0.1° C. of the desired polymerization temperature.
11. The polymerization process of claim 1 , wherein the polymer obtained has a K-value within 0.2 units of the desired K-value.