Production of pearls based on expanded polymers
View Patent ↗Pearls based on expanded polymers are produced by extruding an expandable composition containing a thermoplastic polymer and an expanding agent, and thereafter cooling and chopping the expanded material thus obtained.
1. A process for preparing a pearl comprising an expanded polymer, the process consisting essentially of the following successive steps:
a) extruding an expandable composition comprising a polyamide, as the sole thermoplastic polymer in the expandable composition, and an expanding agent, in molten state, to effect expansion thereof to form an expanded composition, and
b) cooling the expanded composition, using a liquid comprising water, and chopping the cooled expanded composition to form a pearl having a continuous skin and a density of less than or equal to 0.8 g/cm 3 ,
wherein the step of cooling and chopping the expanded composition is performed at the die outlet of the extruder and wherein the prepared pearl is spherical with its largest dimension being less than or equal to 15 mm, and the continuous skin is obtained by performing the above successive steps.
2. The process as defined by claim 1 , wherein the expanding agent comprises a gas that can disperse or dissolve in the polymer melt.
3. The process as defined by claim 1 , wherein the expanding agent comprises a pore-forming agent.
4. The process as defined by claim 1 , wherein the expanding agent comprises a volatile compound that can dissolve in the polymer melt.
5. The process as defined by claim 1 , wherein the expanding agent comprises a chemical compound that can react chemically with the polymer by heating, to generate a gas.
6. The process as defined by claim 1 , wherein the expandable composition comprises a nucleating agent and/or a surfactant and/or a plasticizer.
7. The process as defined by claim 1 , wherein the expandable composition comprises reinforcing fillers.
8. The process as defined by claim 1 , wherein the pearl obtained has a diameter of less than or equal to 10 mm.
9. The process as defined by claim 7 , said reinforcing fillers comprise glass fibers, matting agents, pigments, dyes, heat or light stabilizers, bioactive agents, anti-soiling agents and/or anti-static agents.
10. The process as defined by claim 8 , said diameter being less than or equal to 5 mm.
11. The process as defined by claim 1 , said density being less than or equal to 0.5 g/cm 3 .
12. The process as defined by claim 1 , said density being less than or equal to 0.3 g/cm 3 .
13. The process as defined by claim 1 , wherein the temperature of chopping water is about 85° C.