Dental composition comprising ethylene imine compounds and non-reactive accelerators
View Patent ↗The present invention relates to a composition with enhanced speed of set, especially to a method of making rubber-like elastomers with improved hardening characteristics. In this respect the present invention provides a composition comprising with respect to the cured composition a ethylene imine group containing component A, a SO 2 —NH group containing component B and an initiator C. Optionally additives like modifiers, fillers, dyes, pigments, thixotropic agents, flow improvers, polymeric thickeners, surfactants, odorous substances, diluters and flavorings can be added.
1. A dental composition comprising:
(a) an N-alkyl aziridine polyether,
(b) a compound having an SO 2 —NH group,
wherein component (b) is selected from the group consisting of p-toluene sulfonic acid N-ethyl amide, o-toluene sulfonic acid N-ethyl amide, and a mixture of o-/p-toluene sulfonic acid N-ethyl amide; and
(c) an initiator.
2. A dental composition comprising:
(a) an N-alkyl aziridine polyether,
(b) a compound having an SO 2 —NH group,
wherein component (b) comprises p-toluene sulfonic acid N-ethyl amide; and
(c) an initiator.
3. The composition of claim 1 , further comprising at least one additive selected from the group consisting of modifiers, fillers, dyes, pigments, thixotropic agents, flow improvers, polymeric thickeners, surfactants, odorous substances, diluting agents and flavouring agents.
4. The composition according to claim 1 , wherein component (a) comprises a structural element represented by the following formula:
wherein
R is a moiety selected from the group consisting of H, C 1 -C 12 alkyl, C 2 -C 12 alkenyl, C 2 -C 12 alkinyl, C 7 -C 15 alkylaryl, C 7 -C 15 arylalkyl, and C 3 -C 12 cycloalkyl, wherein any of the hydrogen atoms of the moiety may be replaced by Cl or F and up to five carbon atoms of the moiety may be replaced by atoms or group of atoms selected from O, CO, N, and S, E is selected from the group consisting of C 1 -C 18 branched or unbranched hydrocarbon chains wherein up to five carbon atoms of the chain may be replaced by an atom or group of atoms selected from O, CO, N, and S,
G is a group selected from C(O)O, C(O)NR, C(O), C(O)C(O), C(O)(CH 2 ) m C(O) where m is 1 to 10, C(S)NR, and CH 2 ,
L is O, S, or NR and
x is 0 or 1.
5. The composition of claim 1 , wherein component (b) is o-toluene sulfonic acid N-ethyl amide.
6. The composition of claim 1 , wherein initiator (c) is selected from the group consisting of protonating or alkylating agents or wherein the initiator (c) generates protons or reactive alkylating agents in a chemical reaction.
7. The composition of claim 1 having a working time at 23° C. of equal or less than 3:30 min according to DIN EN ISO 4823:2000 or an oral setting time of equal or less than 3:30 min.
8. The dental composition of claim 1 , wherein the composition is a dental impression material.
9. The dental composition of claim 1 , wherein the initiator comprises an alkyl sulfonium salt.
10. The dental composition of claim 1 , wherein the Shore Hardness A measured after 6 minutes according to DIN EN ISO 53505 is greater than a value measured for the dental composition without component (b).
11. The dental composition of claim 10 , wherein the Shore Hardness A measured after 6 minutes according to DIN EN ISO 53505 is more than 30% greater than the value measured for the dental composition without component (b).
12. A kit comprising a base part and a catalyst part, wherein the base part comprises an N-alkyl aziridine polyether, the catalyst part comprises an initiator, and wherein a compound selected from the group consisting of p-toluene sulfonic acid N-ethyl amide, o-toluene sulfonic acid N-ethyl amide, and a mixture of o-/p-toluene sulfonic acid N-ethyl amide is present either in the base part or the catalyst part or in the base part and the catalyst part
in an amount of about 0.01% by weight to about 6.0% by weight.
13. A kit comprising a base part and a catalyst part, wherein the base part comprises an N-alkyl aziridine polyether, the catalyst part comprises an initiator, and wherein a compound selected from the group consisting of p-toluene sulfonic acid N-ethyl amide, o-toluene sulfonic acid N-ethyl amide, and a mixture of o-/p-toluene sulfonic acid N-ethyl amide is present in a further part in an amount of about 0.01% by weight to about 6.0% by weight and is not present in the catalyst part or in the base part.
14. A method of producing a dental composition comprising the step of mixing
(a) an N-alkyl aziridine polyether,
(b) a compound selected from the group consisting of p-toluene sulfonic acid N-ethyl amide, o-toluene sulfonic acid N-ethyl amide, and a mixture of o-/p-toluene sulfonic acid N-ethyl amide,
present in an amount of about 0.01% by weight to about 6.0% by weight; and
(c) an initiator.
15. A method for enhancing the setting speed of a dental composition, comprising an N-alkyl aziridine polyether, the method comprising the step of incorporating into the composition a compound selected from the group consisting of p-toluene sulfonic acid N-ethyl amide, o-toluene sulfonic acid N-ethyl amide, and a mixture of o-/p-toluene sulfonic acid N-ethyl amide,
present in an amount of about 0.01% by weight to about 6.0% by weight.
16. The kit of claim 12 , wherein the initiator comprises an alkyl sulfonium salt.
17. The kit of claim 13 , wherein the initiator comprises an alkyl sulfonium salt.
18. The method of claim 14 , wherein the initiator comprises an alkyl sulfonium salt.
19. The method of claim 15 , wherein the initiator comprises an alkyl sulfonium salt.