Expandable polystyrene composition
View Patent ↗An expandable polystyrene composition in the form of expandable beads, comprising by weight (1) 100 parts of a styrene polymer, (2) from 2.2 to less than 4.0 parts of at least one blowing agent, and (3) from 0.01 to 0.4 part of at least one plasticizing. The composition is particularly useful for manufacturing medium density expanded moulded polystyrene objects, particularly with a density from 40 to 190 g/l. A process for manufacturing such objects,is provided, together with pre-expanded beads with a buld density of 40 to 190 g/l, containing by weight (a) 100 parts of a styrene polymer, (b) from 0.5 to less than 3.0 parts of at least one blowing agent, and (c) from 0 to 0.4 part of at least one plasticizing agent.
1. Pre-expanded beads having a bulk density chosen from a range of from 40 to 190 g/l and containing by weight:
(a) 100 parts of a polymer of styrene having a mean molecular mass by weight Mw chosen from a range of from 180,000 to 250,000 and a molecular weight distribution calculated by the ratio of Mw to the mean molecular mass by number, M n , in the range of from 2.1 to 2.5,
(b) from 0.5 to less than 3.0 parts of at least one blowing agent,
(c) from 0 to 0.4 part of at least one plasticising agent comprising an oil which is liquid at 20° C., having on average from 25 to 38 carbon atoms, a dynamic viscosity at 25° C. of from 110 to 170 mPa·s and a density of from 0.8 to 0.9, and
(d) less than 400 ppm of residual styrene monomer,
wherein the pre-expanded beads are expandable.
2. Pre-expanded beads according to claim 1 , wherein the blowing agent is chosen from linear or branched (cyclo)alkanes.
3. Pre-expanded beads according to claim 1 , wherein they contain from 0.7 to 2.9 parts by weight of at least one blowing agent.
4. Pre-expanded beads according to claim 1 , wherein they contain from 1.6 to less than 3.0 parts by weight of at least one blowing agent.
5. Pre-expanded beads according to claim 1 , wherein the plasticising agent is selected from the group consisting of mineral oils, white oils, paraffin waxes and Fischer-Tropsch waxes.
6. Pre-expanded beads according to claim 1 , wherein they contain from 0 to 0.35 part of at least one plasticising agent.
7. Pre-expanded beads according to claim 1 , wherein they have a size or a diameter chosen from a range of from 0.5 to 3.5 mm.
8. Pre-expanded beads according to claim 1 , wherein they have a bulk density chosen from a range of from 45 to 180 g/l.
9. Pre-expanded beads according to claim 1 , wherein the pre-expanded beads are capable of subsequent expansion without the addition of a fresh quantity of blowing agent.
10. Pre-expanded beads according to claim 2 , wherein the linear or branched (cyclo)alkanes have from 4 to 6 carbon atoms.